Seriennummer | Spezifikt. Feld | EP-80 | EP-100 | EP-125 | EP-150 | EP-200 | EP-250 | EP-300 | EP-350 | EP-400 | ||||||||||
Gerä T | Verzerrung | einschlag | Verzerrung | einschlag | Verzerrung | einschlag | Verzerrung | einschlag | Verzerrung | einschlag | Verzerrung | einschlag | Verzerrung | einschlag | Verzerrung | einschlag | Verzerrung | einschlag | ||
1 | Feld | dtex | 1100X1 | 930X1 | 1100X1 | 930X1 | 1670X1 | 1400X1 | 1100X2 | 1870X1 | 1100X2 | 1400X2 | 1100X4 | 1870X2 | 1100 X4 | 1870 X2 | 1870 X3 | 1870 X2 | 1870X4 | 1870X2 |
2 | Dichte | radikal /10cm | 155 ± 2 | 76 ± 2 | 194 ± 2 | 86 ± 2 | 170 ± 2 | 72 ± 2 | 166 ± 2 | 56 ± 2 | 186 ± 2 | 44 ± 2 | 120 ± 2 | 38 ± 2 | 146 ± 2 | 38 ± 2 | 150 ± 2 | 38 ± 2 | 125 ± 2 | 38 ± 2 |
3 | Durchschnittliches brechendes strength≥ | N/mm | 100 | 50 | 137 | 55 | 165 | 70 | 206 | 75 | 246 | 85 | 330 | 105 | 350 | 105 | 400 | 105 | 465 | 105 |
Bruchfestigkeit (Minute) ≥ | 95 | 45 | 118 | 50 | 145 | 60 | 176 | 68 | 220 | 75 | 290 | 95 | 320 | 95 | 370 | 95 | 425 | 95 | ||
4 | Dehnung bei dem 10% load≤ | % | 1.5 | 15 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | |||||||||
5 | Dehnung am Bruch | % | ≥ 14 | ≥ 14 | ≤ 45 | ≥ 14 | ≤ 45 | ≥ 14 | ≤ 45 | ≤ 45 | ≥ 15 | ≤ 45 | ≥ 15 | ≤ 45 | ≥ 15 | ≤ 45 | ≥ 15 | ≤ 45 | ||
6 | Trocknende Schrumpfung %≤ (150º C*30min) | % | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 5.0 | 0.5 | 6.0 | 0.5 |
7 | Ungleich trocknendes shrinkage≤ | % | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | |||||||||
8 | Adhä Sion strength≥ | N/mm | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | 7.8 | |||||||||
9 | Gewicht (Gramm pro m2) | g/m2 | 300± 10 | 340± 15 | 425± 20 | 530± 20 | 615± 20 | 780± 30 | 860± 30 | 1000± 35 | 1040± 40 | |||||||||
10 | Stä Rke | mm | 0.55± 0.05 | 0.55± 0.05 | 0.60± 0.05 | 0.70± 0.05 | 0.80± 0.05 | 1.07± 0.10 | 1.20± 0.10 | 1.26± 0.10 | 1.40± 0.10 | |||||||||
11 | Lä Nge | mm | 0 0 800~1400 - 20 -20 | 0 0 800~1500 - 20 -20 | 0 0 800~1500 - 20 -20 | 0 0 800~1550 - 20 -20 | 0 0 800~1600 - 20 -20 ---- | 0 0 800~1600 - 20 -20 | 0 0 800~1600 - 20 -20 | 0 0 800~1600 - 20 -20 | 0 0 800~1600 - 20 -20 |