Complaint
| General specifications | |
| Width mm | Thickness mm |
| 44 | 6.8 |
| 44 | 5 |
| 42 | 1.3 |
| 40 | 4 |
| 31 | 6.8 |
| 31 | 6.5 |
| 31 | 5.5 |
| 30 | 2.5 |
| 18 | 9 |
| 16 | 11 |
| Hot-selling specifications | |
| 31 | 6 |
| 31 | 5 |
| 31 | 3.5 |
| 22 | 3.6 |
| 32 | 4 |
| Glass Fiber + Resin System | Part No | Resin Base | Application | Temperature resistance | Corrossion resistance |
| Flame resistance | VE | Vinyl Ester | Superior Corrosion Resistance and fire retardant | Very Good | Excellent |
| Very Good | ISO | Isophthalic Polyester | Industrial grade corrosion resistance and fire retardant | Good | Good |
| Good | ORTHO | Orthophthalic resin | Moderate corrosion resistance and fire retardant | Common | Common |
| Common | EPOXY | EPOXY Resin | |||
| Item | Normal type | Ordinary high temperature resistant type |
density (g/cm3) | >2.0 | >2.0 |
Water absorption (%) | <0.05 | <0.05 |
Tensile Strength (MPa) | >=1200 | >1200 |
Penetration test (min) | >20 | >20 |
Water diffusion test (mA) | <0.2 | <0.2 |
Stress corrosion (h) | / | / |
V sdc(kv) | >50 | >50 |
Hot bending failure load (MPa) | / | >=230 |
| Item | Acid proof type | Acid and high temperature resistant type |
| density (g/cm3) | >2.0 | >2.0 |
| Water absorption (%) | <0.05 | <0.05 |
| Tensile Strength (MPa) | >=1300 | >1300 |
| Penetration test (min) | >20 | >20 |
| Water diffusion test (mA) | <0.2 | <0.2 |
| Stress corrosion (h) | >96 | >96 |
| V sdc(kv) | >50 | >50 |
| Hot bending failure load (MPa) | / | >=230 |