Chemische Zusammensetzung
Gemeinsame Stahlsorte von Edelstahlrohr / Rohr | |||||||||
Grad | Chemische Zusammensetzung (%) | Mechanieal Performece | |||||||
C | Si | Mn | P | S | Ni | Cr | Andere | Härte | |
201 | ≤0,15 | ≤1,00 | 5,5/7,5 | ≤0,060 | ≤0,030 | 3,5/5,5 | 16,0/18,0 | - | HB≤241, HRB≤100, HV≤240 |
202 | ≤0,15 | ≤1,00 | 7.5/10 | ≤0,060 | ≤0,030 | 4,0/6,0 | 17,0/19,0 | - | HRB≤195, HV≤218 |
304 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 8,0/11,0 | 18,00/20,00 | - | HB≤187,HRB≤90,HV≤200 |
316 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 10,00/14,00 | 16,0/18,0 | Mo:2,00/3,00 | HB≤187, HRB≤90 HV≤200 |
316L | ≤0,03 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 10,00/14,00 | 16,0/18,0 | Mo:2,00/3,00 | HB≤187, HRB≤90 HV≤200 |
321 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 9,00/12,00 | 17,0/19,0 | TI: 5C-0,70 | HRB≤90, HV≤200 |
410 | ≤0,15 | ≤1,00 | ≤1,25 | ≤0,060 | ≤0,030 | ≤0,060 | 11,5/13,5 | - | HB≤183, HRB≤88 HV≤200 |
430 | ≤0,12 | ≤1,00 | ≤1,25 | ≤0,040 | ≤0,03 | - | 16,00/18,00 | - | HB≤183, HRB≤88 HV≤200 |
Oberflächendifferenz
No,1 (warmgewalzt): Nach Warmwalzen, Glühen, Beizen und Dephosphorisation. Die Oberfläche der behandelten Stahlplatte ist eine matte Oberfläche, etwas rau.