Complaint
| Type | CT 23 | CT B5 | CT 26 | CT 28 | CT 30 | CT 32 | |
| Classification temperature ºC | 1250 | 1300 | 1400 | 1500 | 1550 | 1600 | |
| Density (kg/m3) | 500 | 800 | 800 | 900 | 1000 | 1100 | |
| Linear Shrinkage on Reheating (ºCx4h) | 0.4(1200) | 0.4(1300) | 0.5(1400) | 0.7(1500) | 0.7(1550) | 0.7(1600) | |
| Compressive strength (Mpa) | 1.0 | 1.8 | 1.9 | 2.5 | 2.8 | 3.0 | |
| Rupture strength (Mpa) | 0.7 | 1.2 | 1.2 | 1.4 | 1.6 | 1.8 | |
| Thermal Conductivity(W/m.k) | 0.15 (350ºC) | 0.26 (350ºC) | 0.26 (350ºC) | 0.33 (350ºC) | 0.38 (350ºC) | 0.43 (350ºC) | |
| Thermal Conductivity (ºC) | 0.46 (1000ºC) | 0.46 (1000ºC) | 0.47 (1000ºC) | 0.48 (1000ºC) | 0.48 (1000ºC) | 0.49 (1000ºC) | |
| Chemical Compoaition | Al2O3 | 40 | 52 | 56 | 65 | 72 | 78 |
| Fe2O3 | 1.2 | 0.85 | 0.8 | 0.8 | 0.7 | 0.5 | |
Jiangsu Cera Thermal Technology Co., Ltd. is formerly known as Nanjing Cera Material Technology Co., Ltd.The main business of our company includes refractory materials production, furnace lining design and construction of high-temperature thermal engineering, furnaces equipment, research and development and sales of refractory material. Through years of cooperation with the British Morgan Thermal Ceramics, we have accumulated rich experience in a good deal of engineering projects. We can provide our customers with all kinds of high quality products, professional and customized products and engineering services accordingto the actual working condition and requirements of each customer, in order to meet customers' increasing demand of energy-saving.
Our tenet is: quality and credibility is fundamental, technology and service is the life.
We obtained the quality system certification GB/T 19001-2008/ISO 9001:2008.
High-tech enterprises are under declare.
Remark
The values given herein are typical average values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice. Therefore, the data contained herein should not be used for specification purposes.