| C106 Semi-Conductive/Insulation/Elastomeric Insulation Tri-Layer Heat Shrink Tube | ||||
| Features | ||||
| Cross-linked heavy wall tubing | Operating temperature: -55~105ºC | |||
| Tri-layer design with high recovery forces | Shrink temperature: 135-150ºC | |||
| Co-Extrusion technology | Voltage class: 10-35 KV | |||
| Eliminates partial discharge | Halogen free ,RoHs Compliant | |||
| Enable the joint to follow the thermally induced dimensional changes of cable insulation. | ||||
| Dimensions | ||||
| Reference | As supplied(mm) | After recovered(mm) | Standard length | |
| UPM C106 | ID min. | ID max. | WT nom. | m/pc |
| 35/13 | 35 | 13 | 11.0 | 1 or 1.22 |
| 45/17 | 45 | 17 | 12.0 | 1 or 1.22 |
| 50/21 | 50 | 21 | 12.7 | 1 or 1.22 |
| 63/26 | 63 | 26 | 13.5 | 1 or 1.22 |
| 75/34 | 75 | 34 | 13.5 | 1 or 1.22 |
| 85/34 | 85 | 34 | 13.5 | 1 or 1.22 |
| 95/42 | 95 | 42 | 14.2 | 1 or 1.22 |
| 110/52 | 110 | 52 | 14.2 | 1 or 1.22 |
| 125/62 | 125 | 62 | 15.0 | 1 or 1.22 |
| ID=Internal Diameter | WT=wall thickness | |||
| Typical application | ||||
| Ideal for insulation of power cable joint up to 42KV | ||||
| Ordering | ||||
| Standard color : Black/Red/Red | ||||
| Standard packaging is 1m/pc or 1.22m/pc | ||||
| Please specify specification,quantity when ordering | ||||
| Cross reference | ||||
| Raychem/ Tyco: ERIT/ERIC/ERIH | ||||
| Technical Data | |||
| Property | Test method | Joint | |
| Inner layer | |||
| Physical | Tensile strength | ASTM D2671 | ≥6 MPa |
| Breakdown elongation | ASTM D2671 | ≥600% | |
| Aging (136ºC /168hrs) | Tensile strength | ASTM D2671 | ≥4.2 MPa |
| Breakdown elongation | ASTM D2671 | ≥420% | |
| Thermal endurance | IEC 216 | 105 ºC | |
| Water absorption (23ºC/336hrs) | ASTM D570 | ≤0.5% | |
| Density | ASTM D2671 | 0.95~1.05 | |
| Low temperature flexibility(-55ºC/4hrs) | ASTM D2671 | No cracking. | |
| Hardness (Shore D) | ASTM D2671 | ≤ 30 HD | |
| Electrical | Dielectric strength(in insulation oil) | ASTM D 2671 | ≥15KV/mm |
| Volume resistivity | ASTM D 2671 | ≥1014 Ω.cm | |
| Middle layer | |||
| Physical | Tensile strength | ASTM D2671 | ≥12 MPa |
| Breakdown elongation | ASTM D2671 | ≥400% | |
| Aging (136ºC /168hrs) | Tensile strength | ASTM D2671 | ≥12 MPa |
| Breakdown elongation | ASTM D2671 | ≥350% | |
| Thermal endurance | IEC 216 | 105 ºC | |
| Water absorption (23ºC/336hrs) | ASTM D570 | ≤0.5% | |
| Density | ASTM D2671 | 1.05~1.15 | |
| Low temperature flexibility(-40ºC/4hrs) | ASTM D2671 | No cracking. | |
| Heat shock (200ºC/30mins) | ASTM D2671 | No cracking. | |
| Hardness (Shore D) | ASTM D2671 | ≥ 35 HD | |
| Electrical | Dielectric strength(in insulation oil) | ASTM D 2671 | ≥15KV/mm |
| Volume resistivity | ASTM D 2671 | ≥1013 Ω.cm | |
| Outer layer | |||
| Physical | Tensile strength | ASTM D2671 | ≥20 MPa |
| Breakdown elongation | ASTM D2671 | ≥350% | |
| Aging (158ºC /168hrs) | Tensile strength | ASTM D2671 | ≥16 MPa |
| Breakdown elongation | ASTM D2671 | ≥300% | |
| Thermal endurance | IEC 216 | 135 ºC | |
| Water absorption (23ºC/336hrs) | ASTM D570 | ≤0.5% | |
| Density | ASTM D2671 | 1.05~1.10 | |
| Heat shock (250ºC/30mins) | ASTM D2671 | No cracking.No drop, no flow | |
| Low temperature flexibility(-40ºC/4hrs) | ASTM D2671 | No cracking. | |
| Hardness (Shore D) | ASTM D2671 | ≥ 55 HD | |
| Electrical | Volume resistivity | ASTM D 2671 | ≤104 Ω.cm |
| Inner layer & Middle layer & Outer layer | |||
| Halogen free | IEC 61249-2-21 | Cl : 900ppm max. | |
| Br : 900ppm max. | |||
| Total (Cl + Br) : 1500ppm max | |||