Description
PVC compound for generic cable70ºC & 90ºC PVC insulation & sheathing compound PVC bedding & filling compoundPVC compound for plugFR PVC compound for UL cable-20ºC~60ºC FR PVC compound -40ºC~90ºC FR PVC compound-40ºC~105ºC FR PVC compound105°C FR PVC compound for charging cable105°C FR PVC compound for charging cableLow smoke low halogen FR PVC compound70°C LSLH high FR PVC compound90°C LSLH high FR PVC compoundPVC compound for special cableCold resistance UV resistance 105°C FR PVC jacket compound Anti-termite & Anti Rodent PVC compound90°C Oil resistance FR PVC compoundRigid & Soft PVC compoundPVC compound for generic cable70ºC & 90ºC PVC insulation & sheathing compound PVC bedding & filling compoundPVC compound for plugFR PVC compound for UL cable-20ºC~60ºC FR PVC compound -40ºC~90ºC FR PVC compound-40ºC~105ºC FR PVC compound105°C FR PVC compound for charging cable105°C FR PVC compound for charging cableLow smoke low halogen FR PVC compound70°C LSLH high FR PVC compound90°C LSLH high FR PVC compoundPVC compound for special cableCold resistance UV resistance 105°C FR PVC jacket compound Anti-termite & Anti Rodent PVC compound90°C Oil resistance FR PVC compoundRigid & Soft PVC compound1.Technical specifications of 70 ºC pvc compound
Tensile strength | MPa | 20.5 |
Fracture tensile strain | % | 320 |
Ageing temperature | ºC | 100 |
Ageing time | h | 168 |
Tensile strength after ageing | MPa | 22.5 |
Max change of tensile strength | % | +12 |
After ageing fracture tensile strain | % | 290 |
Max change of fracture tensile strain | % | -10 |
Thermal deformation | % | 28 |
Thermal ageing quality loss | g/m2 | 19 |
200ºC thermal stability time | min | 90 |
20ºC volume resistivity | Ω.cm | 2.0*1011 |
Technical specifications of 90 ºC pvc resin compound
Tensile strength | MPa | 20 |
Fracture tensile strain | % | 330 |
Ageing temperature | ºC | 100 |
Ageing time | h | 240 |
Tensile strength after ageing | MPa | 21.5 |
Max change of tensile strength | % | +8 |
After ageing fracture tensile strain | % | 310 |
Max change of fracture tensile strain | % | -6 |
Thermal deformation | % | 28 |
Thermal ageing quality loss | g/m2 | 9 |
200ºC thermal stability time | min | 120 |
20ºC volume resistivity | Ω.cm | 2.0*1010 |
2,Use and standard: wire and cable
3,Process: extrusion
4,Appearance: cylindrical particles, plastication should be good, the color and luster is even, without obvious impurity.
5,color: Any colors, base on requirement.
6,Packing: 25kg net weight or 1000kgs per jumbo bag
7, Transportation and storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.