High Strength SMC Sheet Molding Compound for GRP Water Tank Panel

Min.Order: 100

Product origin: Changzhou, Jiangsu, China

Infringement complaint:

Complaint

US$ 1.15 ~ 1.45

Description

Introduction:
Sheet moulding compound (SMC) or sheet moulding composite is a ready to mould glass-fibre reinforced polyester material primarily used in compression moulding. Alternatively the resin and related materials may be mixed on site when a producer wants greater control over the chemistry and filler.

Sheet moulding compound (SMC) is manufactured by dispersing long strands (usually >1") of chopped fiber (commonly glass fibers or carbon fibers on a bath of thermoset resin (commonly polyester resin, vinyl ester or epoxy resin)). The longer fibers in SMC result in better strength properties than standard bulk moulding compound (BMC) products. Also we provide long and continuous fiber or woven roving for extra reinforcement.

Features:
High mechanical strength, low shrink, low density, dimensional stability, corrosion resistance, fire resistance,

Typical Application:
Electrical applications, corrosion resistant needs, structural components at low cost, automotive, sanitary, transit.

Type	Application
General Purpose	Non-electric products such as chair, water tank
Heat and Corrosion Resistant	Composite materials intended for use in sanitary, such as shower base, bath tub, walls
Electric	Satisfy different flame ratings such as UL94 HB, UL94 V0. High strength, UV stability. Suitable to make electric parts used indoor or outside
High Strength & A Grade Surface	High strength, good tenacity, A grade surface. Suitable to make door skin and auto parts such as bumper, panel, truck high roof

Typical Specification:

Physical Property	Units	Standard	Data	Remark
Specific Gravity	( g/cm³)	ASTM D-792	1.7-1.9	-

Glass fiber content	%	GB/T15568-95	18-40	-

Water absorption	%	ASTM D-570	0.2-0.3	24Hrs@23C

Average Shrinkage	%	ASTM D-955	0.05-0.2	-

Tensile Strength	Mpa	ASTM D-638	62	-

Tensile Modulus	Gpa	ASTM D-638	15	-

Flexural Strength	Mpa	ASTM D-790	158	-

Flexural Modulus	Gpa	ASTM D-790	14	-

Compressive Strength	Mpa	ASTM D-695	185	-

Impact Strength-Izod Notched	J/m	ASTM D-256	640	-

Impact Strength-Izod Unnotched	J/m	ASTM D-4812	854	-

Barcol Hardness	-	ASTM D-2583	30-60	-

Heat Distortion Temp	C	ASTM D-648	>204	264 psi

Flammability	cm/min	ASTM D-635	1.7	Average Burn Rate

Color	-	RAL	7035	-