Al/Ti/CS Clad Plate Sheet Transition Joints

Min.Order: 1
Product origin: Zhengzhou, Henan, China
Infringement complaint: complaintComplaint
US$ 1 ~ 10

Description
AL/TI/CS Clad Plate Sheet Transition Joints

Aluminum has excellent electrical conductivity and thermal conductivity, making it widely used in the electrical industry. Aluminum is non-ferromagnetic, which is an important characteristic for the electrical industry and the electronics industry.


The specific strength of some aluminum alloys is comparable to that of steel, and its specific stiffness exceeds that of steel. Therefore, aluminum alloy materials have been widely used in transportation, chemical industry, machinery, power, electronics and construction, especially in aerospace industry.

The temperature of the joint is usually <300ºC. If titanium is added between aluminum and steel, both AL/TI/CS Clad Plate Sheet Transition Joints are used, the bonding strength and conductivity can remain unchanged when the service temperature reaches 450 ºC.
 
Base plate alloyQ235,Q245R,Q345R,DH36,CCSB 
Middle plate alloyTA1,TA2 
Cladding plate alloy5083, 1060,1070 
StandardCB 1343-98 
Cladding plate thickness≥10mm 
Base plate thickness≥12mm 
Length≤3000mm 
Width≥20mm 

Usage:
1. Aluminum-titanium stainless steel pipe joints are used for the transition connection between the components of large-scale cold mills and the pipes conveying liquid nitrogen and liquid oxygen.

2.AL/TI/CS Clad Plate Sheet Transition Joints used in ship structure construction.

3. Titanium acts as the intermediate layer in the multi-layer composite plate which replaces the flange connection in the cryogenic device, such as the corrosion-resistant aluminum alloy-pure aluminum-titanium-nickel-stainless steel composite plate.