Complaint
| Name | customized transparent acrylic fish jar project price |
| size | drawing from customer design |
| thickness | 20mm to 650mm |
| color | transparent |
| shape | flat cuved base on drawing |
| Material | original LUCITE |
| desity | 1.2 |
| transparency | above 92% |
| standard | GB/T 7134-2008 |
| weight | length (m)x width (m) x thickness(mm) x 1.2 |
| purpose | aquarium project, swimming pool and so on |
| factory | xingcheng aquarium technology |
| place of original | Jiangsu Province China |
| 1 | Overall fully without seam |
| 2 | Good safety performance |
| 3 | Good transparence more thank 92% |
| 4 | Good weather resistance,acid and alkali resistance,high hardness, impact resistance is strong,suitable for installation and special need a safe place |
| 5 | Light weight, half of glass |
| 6 | Easy to clean |
| 1 | Oceanarium, aquarium engineering |
| 2 | leisure bathing |
| 3 | Entertainment performance of waterscape interactive acrylic tank |
| 4 | Museum display tank |
| 5 | Acrylic swimming pool |
| 6 | Large KTV,big club,upscale hotel |
| 7 | Shopping center |
| 8 | Large ecological aquarium for villa |
| 9 | Underwater world acrylic sightseeing tunnel |
| 10 | Acrylic display wall |
| 1 | Acrylic sheet is made by imported material by ourselves, good quality control ability |
| 2 | Own good designing team |
| 3 | Good installation ability,overseas installation capacity |
| 4 | Many years foreign trade experience, good foreign team |
| 5 | Large number of engineering case at home and abroad |
| PROPERTIES | VALUE | Method ASTM | VALUE | Method DIN |
| Density (specific weight) | 1,19 g/cm 3 | D 792 | 1,19 g/cm 3 | 53479 |
| Modulus of elasticity | 32.000 Kg./cm 2 | D 790 | 3200 N/mm 2 | 53457 |
| Tensile Strenght | 740 kg/cm 2 | D 638 | 74 kg/cm 2 | 53455 |
| Flexural Strenght | 1200 kg/cm 2 | D 790 | 120 kg/cm 2 | 53452 |
| Elongation at break | 3,0 % | D 638 | 3,0 % | 53455 |
| Impact Strenght (Izod) | 2,0 kg/cm | D 256 | 2,0 kg/m 2 | 53453 |
| Impact Strenght (Charpy) | 25 kg/cm | D 256 | 27 kg/m 2 | 53453 |
| Rockwell Hardness | M 100 | D 785 | / | / |
| Ball Drop H98/30 | / | / | 200 N/mm 2 | 53453 |
| PROPERTIES | VALUE | Method ASTM | VALUE | Method DIN |
| Coefficient of thermal conductivity | 5,0 10 -4 cal/cm s ° C | C 177 | 0,19 W/m°C | 52612 |
| Deflection temperat.- 1,8 N/mm 2 | 105 °C | D 648 | 105 °C | 53461 |
| Softenig Point (Vicat) | > 115 °C | D 1525 | > 115 °C | 53460 |
| Coef. Linear Thermal Expantion | 7,5 10 -5 1/°C | D 696 | 75 10 -4 1/°C | VDE0304/1 |
| Specific Heat | 0,35 cal/g°C | / | / | / |
| PROPERTIES | VALUE | Method ASTM | VALUE | Method DIN | ||
| Dielectric Strength | 20 kV/mm | D 149 | 20 kV/mm | 53461 | ||
| Volume Resistivity | 1 10 15 Ohm/cm | D 257 | / | / | ||
| Surface Resistivity | 1 10 14 Ohm | D 257 | 1 10 14 Ohm | 53482 | ||
| Transversal Resistivity | > 10 15 Ohm/cm | D 257 | ||||
| Dielectric Constant (50 Hz) | 3,5 | D 150 | 3,5 | 53483 | ||
| Power Factor (50 Hz) | 0,05 | D 150 | 0,06 | 53483 | ||
| PROPERTIES | VALUE | Method ASTM | VALUE | Method DIN |
| Refractive Index n 20 D | 1,49 | D 542 | 1,49 | 53491 |
| Light Transmittance | 92% | D 1003/A | 92 % | 5036 |
| Turbidity (Haze) | 0,5% | D 1003/A | / | / |
| PROPERTIES | VALUE | METHOD |
| Medium molecular weight | 800 - 1000 10 3 uma | viscous |
| Resistance to acids | good | / |
| Resistance to bases | good | / |
| Resistance to chlorous solvents ( methylene chloride, chloroform, trichloroethylene etc.) | low | / |
| Resistance to non chlorous solvents (acetone,alcohol, petrol, etc.) | medium | / |
| PROPERTIES | VALUE | METHOD |
| Flame propagation | 22 - 28 mm/min. | ASTM D635/63 |
| Igniting T. | 280 - 300 °C | ASTM D 93 |
| Autoigniting T. | 425 °C | DIN 51794 |
| Calorific power | 6600 kcal/kg | / |
| Oxygen index | 18 | ASTM D28/63 |
| Flammability | class B2 | DIN 4102 |
| Smoke density (Flamming) | Dm 50 | NBS |
| PROPERTIES | VALUE | METHOD |
| Water absorption rate | 30 mg | ISO 62, m.l |
| Max % increase of weight after water immersion | 2,1% | ISO 62, m.l |
| Coef.of steam permeability | 2,3 10 -10 g/cmPa | / |
| Coef.of N2 permeability | 4,5 10 -15 g/cmPa | / |
| Coef.of O2 permeability | 2,0 10 -14 g/cmPa | / |
| Coef.of CO2 permeability | 1,1 10 -13 g/cmPa | / |
| Coef. of air permeability | 8,3 10 -15 g/cmPa | / |