Complaint
| No | Item | The standard | Test result | |
| 1 | Appearance | Have no grain, no agglomerations, no skinning, no bubble. | Pass the standard | |
| 2 | Droop degree mm | Uprightness | ≤3 | 0 |
| Level | Not change shape | Not change shape | ||
| 3 | Extrusion (s) | ≤10 | 2 | |
| 4 | Skinning time/h | ≤3 | 0.5 | |
| 5 | Hardness (HsA) | 20~60 | 46 | |
| 6 | 23ºCTensile modulus Mpa | 10% Tensile h/kPa | / | 288.7 |
| 20% Tensile h/kPa | / | 442.1 | ||
| 40% Tensile h/kPa | / | 620.6 | ||
| 7 | Tensile adhesion capability | at 23ºC Tensile strength in Adhesion (Mpa) | ≥0.60 | 1.02 |
| Adhesion broken area (%) | ≤5 | 0 | ||
| Elongation at Ultimate Strength (%) | ≥100 | 173 | ||
| at 90ºC Tensile strength in adhesion (Mpa) | ≥0.45 | 0.76 | ||
| Adhesion broken area (%) | ≤5 | 0 | ||
| At -30ºC C12 Tensile strength in Adhesion (Mpa) | ≥0.45 | 1.49 | ||
| Adhesion broken area (%) | ≤5 | 0 | ||
| After flooding Tensile strength in Adhesion (Mpa) | ≥0.45 | 0.86 | ||
| Adhesion broken area (%) | ≤5 | 0 | ||
| After UV radiation Tensile strength in adhesion(Mpa) | ≥0.45 | 0.84 | ||
| Adhesion broken area (%) | ≤5 | 0 | ||
| 8 | Aging test | TG (%) | ≤10 | 4.2 |
| cracking | NO | NO | ||
| efflorescence | NO | NO | ||