Complaint
| Item | CL-HFT | |
| Continuus Temperature Range | -40ºC-125ºC | |
| Radial Shrinking Ratio | 2:1 3:1 | |
| Longitudinal Shrinking Ratio | ±5% | |
| Tensile Strength | ≥10.4MPa | |
| Elongation Ratio | ≥200% | |
| Aging in circulating-air oven | (158±1.0)ºC,7days | |
| After aging | Tensile Strength | ≥7.3MPa |
| Elongation Ratio | ≥100% | |
| Dielectric Voltage Withstand | 600V | |
| Corrosion of Bare Copper | ≥15kV/mm | |
| Flammability | VW-1 | |
| Concentricity | ≥65% | |
| inner diameter | wall thickness | shrink ratio | inner diameter after recovering |
| φ15 | 0.4mm | 2:1 | <7.5 |
| φ15 | 0.7mm | 2:1 | <7.5 |
| φ15 | 0.85mm | 2:1 | <7.5 |
| φ16 | 0.7mm | 2:1 | <8 |
| φ18 | 0.4mm | 2:1 | <9 |
| φ18 | 0.7mm | 2:1 | <9 |
| φ20 | 0.5mm/0.7mm | 2:1 | <10 |
| φ25 | 0.5mm/0.7mm | 2:1 | <12.5 |
| φ30 | 0.5mm/0.7mm | 2:1 | <15 |
| φ35 | 0.5mm/0.7mm | 2:1 | <17.5 |
| φ40 | 0.5mm/0.7mm | 2:1 | <20 |
Special specifications, wall thickness can be customized.