Complaint
| Material Property | 100% PVA Fiber |
| Breaking Strength | 1600Mpa |
| Color | Light Yellow |
| Crack Elongation | 7.2% |
| Diameter | 15um |
| Initial Modules | 34Gpa |
| Length | 3/6/9/12/18mm(customize cut) |
| Dry Fracture Elongation | 6.8% |
| Light Resistance | better than other fibers |
Polyvinyl alcohol fiber with high strength and high modulus polyvinyl alcohol (PVA) as the main raw material, made by wet spinning process. The product has a high modulus, high strength, low elongation, pollution-free, non-toxic, and with acid, alkali, salt, abrasion, sunlight, corrosion, enzymes borers, cracking, anti-penetration, anti-UV, antiaging properties. The essential characteristic of these reinforcements is to absorb and distribute throughout the entire length - and thus attenuate - the tensions that are created in the material by an external load applied to the object.
Performance
1. With the purpose of high modulus, high strength, alkali and acid resistance, heat resistance. It Also has macromolecule material.
2. Mainly be used in construction, cement industry, non asbestos material for heat and attrition resistance, plastic and rubber reinforcement.
3. It is the good substitution of Asbestos.
Specification
| Material | Polyvinyl Alcohol |
| Fiber Type | Filament |
| Diameter | Around 15.0 um |
| Color | Light Yellow |
| Breaking Strength | Around 1600MPa |
| Dry Breaking Tenacity(cn/dtex)≥ | 11 |
| Dry Breaking Elongation% | 6.0-8.0 |
| E-Modulus (cn/dtex)≥ | 290 |
| Hot water resistanceºC≥ | 104 |
| Length mm | M+ -0.5 |
| Dispersion, grade | 1~3 |
| Note: M denotes 4mm, 5mm, 4-6mm, 6mm, 8mm | |