APP-Modified Bitument Waterproofing Membrane

Min.Order: 3,000

Product origin: Beijing, China

Infringement complaint:

Complaint

US$ -1

Description

APP-PYPE
APP-Modified Bitumen Waterproof Membrane with Polyester Fiber and PE Film

Description
APP-PYPE is a waterproofing modified bitumen base sheet consisting of
atactic polypropylene (APP) or amorphous poly-α-olefin (APAO, APO)
modified asphalt reinforced with polyester fiber covering with polyet-
hylene surfacing. There have three kinds of thickness: 3 mm, 4 mm and 5 mm.

Where to use

Roofs or undergrounds;
Pools, such as swimming pools, fire pools;
Subways, tunnels, concrete road or bridge surfaces;
Sewage plants, garbage burying projects;
Penstocks.

Advantages

The combination of polyester fiber and APP modified bitumen is showed excellent performance on waterproofness;
It will be a high-strength membrane to resist water;
Puncture-resisting, tear-resisting, corrosion-resisting, mould-resisting and weather-resisting;
Excellent tensile strength and elongation;
Strong adaptability for substrate shrinkage, deformation and cracks;
High temperature resistance(130° C);
Convenient to apply: use heat fusion method in all seasons.

Standards
EN 13707

Storage
APP-PYPE material should be stored in well-ventilated shade place and protected from sun or rain. The temperature in stored places can not be higher than 50° C. It only can be put vertically in single-level. The normal shelf life is 1 year.

Transportation
APP-PYPE material can not be inclination or lateral drift. Cover with cloth when it is necessary.

Application System
Yuhong modified bitumen membrane waterproof system includes substrate, undercoat, membrane waterproof layer, protection and isolation layer.
Yuhong also provide a complete line of compatible accessories and components, including primers, adhesives for membrane, pipe clamps, terminal battens and screws.

Application Method
Surface preparation
Surfaces should be dry, clean, smooth and free from any dusts, oil or loose particles. Cracks and surface irregularities need to be filled by polymer mortar.
Priming
Before membrane laying, substrate treating agent need to be brushed evenly and completely cover all laying places.
Membrane Laying
For adhesion between membrane and substrate or membranes, it can use hot melt method or cold adhesion method. According to application designs and specific applied parts, it can be applied by fully adhered method, strip adhered method and border adhered method.
Sealing, fixing and constraining on vertical surfaces
On vertical surfaces, fix with metal battens and seal with sealants for membranes.
Application on protection and isolation layer
After membrane laying, apply on protection and isolation layer according to waterproof layer design.

Item					Units	Requirements	Test Method
Visible defects					-	Visible defects	EN 1850-1
Thickness					mm	≥3.0	EN 1849-1
Mass per unit area		3 mm			Kg/m2	≥3.3	EN 1849-1
		4 mm				≥4.3
		5 mm				≥5.3
Length					m	10±0.01	EN 1848-1
Width					m	1±0.01	EN 1848-1
Straightness					mm/10 m	≤20	EN 1848-1
Maximum tensile force				Longitudinal	N/50 mm	≥800	EN 12311-1
				Transversal		≥800
Elongation at the maximum tensile force				Longitudinal	%	≥35	EN 12311-1
				Transversal		≥35
Maximum peel resistance of joint					N/50 mm	≥75	EN 12316-1
Average peel resistance of joint						≥50
Resistance to tearing(nail shank)					N	≥250	EN 12310-1
Dimensional stability					%	±0.6	EN 1107-1
Shear resistance of joint					N/50 mm	≥400	EN 12317-1
Flexibility at low temperature					° C	-15	EN 1109
Water tightness					k Pa	≥60	EN 1928
Flow resistance at elevated temperature					° C	130	EN 1110
Resistance to impact					mm	2000	EN 12691
Resistance to static loading					kg	15	EN 12730
Artificial ageing behavior	Determination of visible defects		Blister		-	No blister	EN 13707 EN 1297 EN 1850-1
			Crack		-	No crack
			Hole		-	No hole
			Nake spots		-	-
Reaction to fire						Class E	EN ISO 11925-2 EN 13501-1