Description
PRODUCT DESCRIPTION:
LY-5010 is a mixture consisting of polyether polyols, crosslinker, water, silicone stabilizer and catalyst. It is suitable for production of high resilience foam in automotive and furniture markets in conjunction with LY-8501. The typical application density(core) ranges from 45~55
kg/m 3 .
Typical properties| | Part A | Part B |
| Appearance | Milk white viscous liquid | Dark brown transparent liquid |
| Hydroxyl value mgKOH/g | 45±10 | / |
| Dynamic viscosity(25ºC)mpa.s | 1200±200 | 10±5 |
| Density(20ºC) g/ml | 1.05±0.05 | 1.22±0.05 |
| Storage temperature ºC | 15-25 | 15-25 |
| Pot life month | 6 | 12 |
Reactivity Property(Material Temperature is 20ºC)| | Manual | Machine |
| Cream time s | / | / |
| Gel time s | / | / |
| Mould temperature ºC | / | / |
| Demould time min | / | / |
Typical foam performance| Physical properties | Unit | Standard | Test result |
| Ratio(LY-5010A/LY-5010B) | - | - | 1/0.6 | 1/0.65 | 1/0.7 |
| Core density | Kg/m3 | 40--60 | / | / | / |
| Rebound | % | ≥50 | / | / | / |
| Tensile Strength | KPa | / | / | / | / |
| Elongation at break | /% | / | / | / | / |
| Tear Strength | N/cm | / | / | / | / |
| 75% compression set (70ºC,22h) | % | / | / | / | / |
Indentation
Load
Deflection | At 25% | kgf | / | / | / | / |
| At 65% | kgf | / | / | / | / |
| Sag ratio | - | / | / | / | / |
*For information purpose only, not specification
Package
200 liter iron drums, 200kg/drum
Storage
Hygroscopic. Use dry nitrogen or low dew point air for tank padding. Keep drums tightly closed to prevent contamination. Store at 15~25 . Observe all federal, state and local regulations when storing this substance. Store away from incompatible substances.