2. Nano hybrid technology DX. Universal composite is applying unique nano hybrid dispersion technology to maximize
the load of fillers by controlling the size and distribution of particles. It dramatically increased
composite's physical properties and notably improved the smooth surface of restoration in
comparison with traditional micro hybrid or hybrid composite3. Other advantages
• High radiopaque.
• Fluoride releasing to prevent recurrent caries.
• Excellent handling.
Physical Property Comparison
| | DX. Universal nano hybrid | Hybrid/ micro hybrid |
| Filler Size | 0.02-1 um | 0.4-5 um |
| Flexural Strength | 135 Mpa | 80-1 10 Mpa |
| Shrinkage | 2.2% | 2.5-3.5% |
| Filler Load | 77% -83% Wt | 60-70% Wt |
| Polishing Feature | Good | Not Good |
| Wear Resistance | Good | Not Good |
Package:REFILL:
Light Cure Composite: 4g/Syringe*5
Total Etching Adhesive: 5ml/Bottle*1
Etching Gel: 2.5ml/Syringe*1
Syringe Needles : 5pcs/ box*1
Applicators Brushes: 20pcs/box*1
Net weight:188.4g
COLOR: A1,A2,A3,A3.5,B1More ShowDescription of Dental Light Cure Composite Kit:(1)Preparation: isolate and prepare tooth.
(2)Cleaning: rinse the preparation with water.
(3)Drying: gently air dry until there is no visible water.Do not allow enamel or dentin to dry for an excessive period of time.
(4)Applying Dentex Self-Etching Light Cure Adhesive (DSA): dispense 1-2 drops of DSA into a mixing well, apply enough DSA to the entire preparation with a little brush until a shiny surface is achieved and then wait for 10 seconds (DSA should not be applied too much ). Use a gentle stream of air to evaporate the solvent for 5 seconds. (If using a non self-etching adhesive, an etching step should be used according to the manufacturer's instruction).
(5)Cure: light cure for 20 seconds at 500±50mW/cm2. Keep the distance to exposure surface less than 4 mm.
(6)Applying Dentex light cure composite (DLC): place selected DLC into
cavity preparation following by light cure. According to following table, the curing time is recommended for different depth and color shades. In order to reduce shrinkage stress, for a large cavity, an increment filling is recommended. In general, 1-2 mm increments are placed into cavity preparation from different sides and the restoration is built incrementally. Each increment is light cured for 30 seconds.
(7) Finishing: after light cure, adjust restoration.
(8) Polishing: use polishing strip or disc to polish the surface