Complaint
Properties | Test Method | Test Value | ||||||||
| 0.5 mm | 0.75mm | 1.00 mm | 1.25 mm | 1.50 mm | 2.00 mm | 2.50 mm | 3.00 mm | |||
| Maximum Deviation of thickness | -15% | -15% | -15% | -15% | -15% | -15% | -15% | -15% | ||
| Density (min. ave.) | D 1505/D792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | |
| Tensile Properties(min.ave) | Yield strength Break strength | D6693 | 8N/mm | 11 N/mm | 15 N/mm | 18 N/mm | 22 N/mm | 29 N/mm | 37 N/mm | 44 N/mm |
| 14N/mm | 20N/mm | 27 N/mm | 33 N/mm | 40 N/mm | 53N/mm | 67 N/mm | 80 N/mm | |||
| Yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | 12% | ||
| Break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | 700% | ||
| Tear Resistance (min. ave.) | D 1004 | 63 N | 93 N | 125 N | 156 N | 187 N | 249 N | 311 N | 374 N | |
| Puncture Resistance (min. ave.) | D 4833 | 160N | 240N | 320 N | 400 N | 480 N | 640 N | 800 N | 960 N | |
| Carbon Black Content (range) | D 4218 | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | |
| Oxidative Induction Time (OIT) (min.ave.) Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | |
| Oven Aging at 85°C Standard OIT (min. ave.) - % retained after 90 days | D 5721 D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | 55% | |
| UV Resistance High Pressure OIT (min. ave.) - % retained after 1600 hrs | D 3895 D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | 50% | |
| Test Properties | Unit | Standard | Test frequency | GM10 | GM15 | GM20 | GM25 |
| Thickness | mm | D5994 | per roll | 1.00 | 1.50 | 2.00 | 2.50 |
| Asperity Height | mm | D7446 | Every 2nd roll (2) | 0.25 | |||
| Density | g/cc | D1505/D792 | 90,000kg | 0.94 | |||
| Tensile Properties | |||||||
| Yield Strength | KN/m | D6693 Type IV | 9,000 kg | 15 | 22 | 29 | 37 |
| Break Strength | KN/m | 10 | 16 | 21 | 26 | ||
| Yield Elongation | % | 12 | 12 | 12 | 12 | ||
| Break Elongation | % | 100 | 100 | 100 | 100 | ||
| Tear Resistance | N | D1004 | 20,000kg | 125 | 187 | 249 | 311 |
| Puncture Resistance | N | D4883 | 20,000kg | 267 | 400 | 534 | 667 |
| Stress Crack Resistance | hr | D5397(App) | per GRI GM-10 | 300 hr | |||
| Carbon black content | % | D4218 | 9,000kg | 2.0-3.0% | |||
| Carbon black dispersion | / | D5596 | 20,000kg | For 10 different views: 9 in Categories 1 or 2 and 1 in Category 3 | |||
| Oxidative Induction Time | |||||||
| Standard OIT | min | D3895 | 90,000kg | 100 min | |||
| High pressure OIT | / | D5885 | 90,000kg | 400 min | |||
| Oven Aging at 85°C retained after 90 days | % | D5721 | per each formulation | 55% | |||
| Standard OIT | / | D3895 | 80% | ||||
| High pressure OIT | / | D5885 | 80% | ||||
| UV Resistance | |||||||
| High Pressure OIT - % retained after 1600 hrs | % | D5885 | per each formulation | 50% | |||
| Roll Width | m | / | / | 7 | 7 | 7 | 7 |
| Roll Length | m | / | / | 210 | 140 | 105 | 70 |
| Size stability | % | / | / | 2% | |||