Product Paramenters | |
Brand Name | Yuanxian Polymer |
Product Name | Biodegradable Stretch Film / Hand Roll Stretch Film |
Material | PLA+PBAT |
Color | Customized |
Size | Thickness range: 10-30 micorn Width range: 30-60 cm Length range: 15m-10000m Packaging choice: in roll with paper core |
Features | Raw material: PLA + PBAT 100% compostable and biodegradable Good self stickiness, no glue Excleeent performance for pallet wrapping |
Application | Used in airport packing or logistics packing |
Our Advantage | 1. Professional ODM&OEM experience. |
2. Professional equipment produces high quality products. | |
3. Customer success plan. | |
4. Experience Focusing on the R&D of plastic products. | |
5. Fast delivery time. | |
6. 100% safe payment. |
NAME | BINDING USE STRETCH FILM | MANUAL USE WRAPPING FILM | MACHINE USE WRAPPING FILM |
SPECIFICATION ( W x L ) ( Thickness ) | 10 cm x150 m 13 micon | 45 cm x 400 m 20 micon | 50 cm x 1000 m 23 micon |
PACKING WAYS | 40 rolls / carton | 4 rolls / carton | 1 roll / carton |
OUTTER CARTON DIMENSION | 32 x 26 x 22.5 cm | 25 x 25 x 47.5 cm | 21.5 x 21.5 x 53 cm |
PAPER CORE SIZE | 30 mm | 50 mm | 76 mm |
Modified Material
Film Blowing Grade YPMH-S200
Film Blowing Grade PLA Modified Material
PLA+PBAT+STARCH
Item Code: YPMH-S200
Recommended application
Shopping vest bag, wrist bag, roll bag, food preservation bag; Electronic product packaging film, household
Appliance packaging film, medical hygiene film, etc.
Product characteristics
1) Good coloring performance, stable melt strength, and can be directly processed into various films;
2) It is usually light white or light yellow, has fragrance, is easy to be decomposed by microorganisms, and has natural antistatic property;
3) Good heat stability of raw materials, good recyclability of leftover materials, high temparature and strong shear force;
4) This product has low moisture content. It is vacuum packed and can be used after opening.
Material properties
Item | Test method | Conditions for item | Unit | Result[1] |
Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 4.0-7.0 |
Density | 1S0 1183 | 23ºC | g/cm3 | 1.27-1.32 |
Melting point | DSC | - | ºC | 110-130 |
Temperature | Typical value[2] | Reference range | |
Melting temperature | 120ºC | 115-125ºC | |
Temperature of film blowing heating area | Posterior segment | 025ºC | 120-130ºC |
Middle segment | 130ºC | 125-135ºC | |
Anterior segment | 135ºC | 130-140ºC | |
Mould head temperature | 135ºC | 130-140ºC | |
Upper limit of processing temperature | 180ºC |
Characteristics[4] | Test method | Conditions for testing | Unit | Typical values[5] |
Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 21/12 |
Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 250/600 |
Dart impact | 1S0 7765-1 | 25ºC | g | 150 |
Item | Test method | Conditions for item | Unit | Result[1] |
Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 3.0-6.0 |
Density | 1S0 1183 | 23ºC | g/cm3 | 1.38-1.43 |
Melting point | DSC | - | ºC | 110-130 |
Temperature | Typical value[2] | Reference range | |
Melting temperature | 125ºC | 120-130ºC | |
Temperature of film blowing heating area | Posterior segment | 145ºC | 140-150ºC |
Middle segment | 145ºC | 140-150ºC | |
Anterior segment | 150ºC | 140-150ºC | |
Mould head temperature | 150ºC | 140-150ºC | |
Upper limit of processing temperature | 190ºC |
Characteristics[4] | Test method | Conditions for testing | Unit | Typical value[5] |
Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 17/13 |
Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 300/500 |
Dart impact | 1S0 7765-1 | 25ºC | g | 190 |
[3]Typical films are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;
[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;
[5]The above data are typical values, not guaranteed values.