Description
our material
The Lactic acid monomer is made from fermented plant starsh such as from corn.
Polylactic acid (PLA) can be completely decomposed into carbon dioxide (CO2) and water (H2O) under natural conditions after being discarded.
Item No: YPRX-PLA01
Molecular Formula: H-[OCHCH3CO]n-OH
CAS NO: 26100-51-6
Color: White
Standard: GB/T 29284-2012
Monomer content and D-content | % | ≤0.3 |
Density | g/cm3 | >1.24 |
Particle Diameter | mm | 2 |
Melt index (190-C/2.16kg) | g/10min | 10 |
Melt point | ºC | >165 |
Tensile Strength at Break | MPa | >45 |
Elongation at break | % | >5 |
Tensile Modulus | GPa | 6.5 |
Notch Impact Strength | kJ/m2 | >4 |
HDT(0.45Mpa) | ºC | >100 |
Bending strength | Mpa | >70 |
Transmittance | % | >95 |
Degradation Rate | % | >95 |
PLA can be made into film products with high transparency, good barrier properties, excellent processability and mechanical properities, and can be used for flexible packaging of fruits and vegetables.PLA objects can be fabricated by 3D printing, casting, injection moulding, extrusion, machining, and solvent welding.PLA can form a weekly acidic environment on the surface of the product. It has a basis for antibacterial and antifungal. If other antibacterial agents are used in addition, it can achieve an antibacterial rate of more than 90%, and can be used for antibacterial packaging of products. Item | Unit | PP | GPP | PET | PLA |
Density | g/cm3 | 0.9-0.91 | 1.04-1.09 | 1.3-1.4 | 1.25 |
Melt Index | g/10min | 0.2-20 | 1.5-30 | -- | 1-30 |
Tensile strength | MPa | 29.6-35 | ≥58.8 | ≥60 | ≥50 |
Elongation | % | 200-700 | 1.0-2.5 | 30-70 | ≥5 |
Transmittance | % | 85-88 | 88-92 | 90-92 | 90-95 |
PBS
Polybutylene succinate
Item No: YPRX-PBS01, YPRX-PBS02
Molecular Formula: HO-(CO-(CH2)4-CO-O-(CH2)4-0)n-H
CAS NO: 25777-14-4
Standard: GB/T 30294-2013
Color: Natural white
Raw Material: BDO(1,24-butanediol) Succinic Acid
Application: injection molding tablewares and cutlery textile, fishing net, engineering components medical applications, etc.
PBS is biodegradable and environment-friendly material.
Our PBS has excellent mechanical properties, close to PP and ABS plastics; The heat resistance is good, the thermal deformation temperature is close to 100 centigrade, and the service temperature after modification can exceed 100 centigrade.
PBS is widely used in packaging (including food packaging, cosmetic bottles, drug bottles), tableware, disposable medical supplies, agricultural film, pesticide and fertilizer slow-release materials, biomedical polymer materials and other fields. It can not only meet the demand through petrochemical products, but also produce natural renewable crop products such as cellulose, diary by-products, glucose, fructose and lactose through biological fermentation, so as to realize green circular production from nature and return to nature.
No | Item | Unit | YPRX-PBS01 | YPRX-PBS02 |
1 | Density, 25ºC | Standard value | g/cm3 | 1.25 |
Deviation | +0.03 |
2 | Density, 25ºC | ºC | 105-116 |
3 | MFR | Standard value | g/10min | ≤10 | 10-20 |
Deviation |
4 | Moisture | % | ≤0.2 |
5 | Hydroxyl content | mol/t | ≤50 |
6 | Color value | L value | Standard value | -- | ≥75 |
A value | Nominal value | -- | ≤5 |
Deviation | +0.5 |
B value | Nominal value | -- | ≤11 |
Deviation | +1 |
7 | Breaking tensile strength | Mpa | ≥25.0 |
8 | Tensile strain at breaking | % | ≥150 |
9 | Bending strength | Mpa | ≥25.0 |
10 | Bending modulus | Mpa | ≥400 |
PBAT (short for polybutylene adipate terephthalate) is a biodegradable random copolyme, specifically a copolyester of adipic acid, 1,4-butanediol and terephthalic acid(from dimethyl terephthalate).
It is generally seen as a fully biodegradable alternative to low-density polyrthylene, having many similar properties including flexibility and resilience, which makes it ideal for blending with another biodegradable polymer, allowing it to be used for many similar uses such as plastic bags and wraps.
No | Item | Unit | Value |
1 | Density, 25ºC | g/cm3 | 1.23+0.03 |
2 | Melting Point, pm | ºC | 110-145 |
3 | MFR | g/10min | 2.5-4.5 |
4 | Moisture | % | ≤0.1 |
5 | Hydroxyl content | mol/t | ≤50 |
6 | Color value | L value | Standard value | -- | ≥70 |
A value | Nominal value | -- | ≤5 |
Deviation | +1 |
B value | Nominal value | -- | ≤10 |
Deviation | +1 |
7 | Breaking tensile strength | Mpa | ≥15 |
8 | Tensile strain at breaking | % | ≥500 |
9 | Bending strength | Mpa | ≥3 |
10 | Bending modulus | Mpa | ≥30 |
11 | Vicat softening point A50 | ºC | ≥80 |
12 | Ash content | % | ≤0.1 |
MODIFIED MATERIALS
Modified Material
Film Blowing Grade YPMH-S200
Film Blowing Grade PLA Modified Material
PLA+PBAT+STARCH
Item Code: YPMH-S200
Recommended application
Shopping vest bag, wrist bag, roll bag, food preservation bag; Electronic product packaging film, household
Appliance packaging film, medical hygiene film, etc.
Product characteristics
1) Good coloring performance, stable melt strength, and can be directly processed into various films;
2) It is usually light white or light yellow, has fragrance, is easy to be decomposed by microorganisms, and has natural antistatic property;
3) Good heat stability of raw materials, good recyclability of leftover materials, high temparature and strong shear force;
4) This product has low moisture content. It is vacuum packed and can be used after opening.
Material properties
Item | Test method | Conditions for item | Unit | Result[1] |
Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 4.0-7.0 |
Density | 1S0 1183 | 23ºC | g/cm3 | 1.27-1.32 |
Melting point | DSC | - | ºC | 110-130 |
[1]The above data are measured values, not guaranteed values.Processing parameters Temperature | Typical value[2] | Reference range |
Melting temperature | | 120ºC | 115-125ºC |
Temperature of film blowing heating area | Posterior segment | 025ºC | 120-130ºC |
Middle segment | 130ºC | 125-135ºC |
Anterior segment | 135ºC | 130-140ºC |
Mould head temperature | | 135ºC | 130-140ºC |
Upper limit of processing temperature | | 180ºC | |
[2]The above data are typical values and aer only for reference. In the actual processing process, the parameters can be adjusted appropriately.Typical film properties[3] Characteristics[4] | Test method | Conditions for testing | Unit | Typical values[5] |
Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 21/12 |
Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 250/600 |
Dart impact | 1S0 7765-1 | 25ºC | g | 150 |
[3]Typical film are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;[5]The above data are typical values, not guaranteed values.Modified MaterialFilm Blowing Grade YPMH-M300Film Blowing Grade PLA Modified MaterialPLA+PBAT+STARCHItem Code: YPMH-M300Recommended applicationsShopping vest bag, wrist bag, roll bag, food preservation bags; packaging film for electronic products, packaging film for home appliances, medical sanitary films, etc.Product Features1) Independent corn tachnology, high product strength, more than 30% higher than the tensile strength of conventional commercial products;2) Good coloring performance, stable melt strength, and can be directly processed into various films;3)It is usually light white, fragrant, easy to be decomposed by microorganisms, and has natural antistatic property;4)The raw materials have good thermostability, good recyclability of leftover materials, and can withstand high temperature and strong shear force.Material properties Item | Test method | Conditions for item | Unit | Result[1] |
Melt flow rate | 1S0 1133 | 190ºC, 2.16kg | g/10min | 3.0-6.0 |
Density | 1S0 1183 | 23ºC | g/cm3 | 1.38-1.43 |
Melting point | DSC | - | ºC | 110-130 |
[1]The above data are measured values, not guaranteed values.Processing parameters Temperature | Typical value[2] | Reference range |
Melting temperature | | 125ºC | 120-130ºC |
Temperature of film blowing heating area | Posterior segment | 145ºC | 140-150ºC |
Middle segment | 145ºC | 140-150ºC |
Anterior segment | 150ºC | 140-150ºC |
Mould head temperature | | 150ºC | 140-150ºC |
Upper limit of processing temperature | | 190ºC | |
[2]The above data are typical values and are only for reference. In the actual processing process, the parameters can be adjusted appropriately.Typical film properties[3] Characteristics[4] | Test method | Conditions for testing | Unit | Typical value[5] |
Tensile strength longitudinal/transverse | 1S0 527 | 25ºC | MPa | 17/13 |
Elongation at break longitudinal/transverse | 1S0 527 | 25ºC | % | 300/500 |
Dart impact | 1S0 7765-1 | 25ºC | g | 190 |
[3]Typical films are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;
[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;
[5]The above data are typical values, not guaranteed values.
DAGRADATION PROCESS
Biodegradable bags refer to plastic bags that can be completely degraded under specific conditions. They are usually made of biodegradable materials such as polylactic acid (PLA) and polyester (PBAT), which reduce their stability during production and make them easier to degrade in the natural environment without residues.
Compared with ordinary plastic bags, biodegradable bags have the advantages of environmental protection and sustainability. The degradation process refers to the decomposition of polymer molecules into small molecules through microbial action, hydrolysis, oxidation, and other methods, ultimately forming natural substances such as carbon dioxide, water, and organic matter. The degradation products are carbon dioxide and water, which can be directly absorbed by plants in the soil, returned to the soil, or entered the general environment, and can be degraded without polluting the environment.
FAQ
1. Q: What's your main material?
Our main materials are PLA,PBS,PBAT and Corn Starch. The materials are 100% Compostable and Biodegradable, they can be degraded into H20 and C20 completely.
2. Q: What information should I let you know if I want to get a quotation?
The size of the products (Length x Width), if your bag's have the gusset, also please provide the gusset size.
We usually quote you within 24 hours after we get your inquiry. If you are in urgency to get the quotation,please call us or tell us in your mail, so that we could regard your inquiry in priority.
3. Q: The printing: How many colors printing in 1 side or 2 sides?
It will be very useful if you can provide your bag's picture. Of course, samples will be best.
4. Q: What's your MOQ?
Usually 1 tons each kind, the more the cheaper.
5. Q: What is the bag size?
You can measure the length, width and height of the goods that need to packing, we will help you calculate the required size of the bag.
We do customized products, any size & any color we can make according to your requirement.
6. Q: Can you design for me?
According to your requirement, we can add your company logo, website, phone number or your ideas on the bag....
Any color is available. Our profession designer can make design it to for you for free.
Welcome to contact with us for more details!