High Silica Fiberglass Fabric is made by silica fiberglass fabric which is a kind of inorganic fiber contaiting more than 96% SiO2. It is high temperature resistance. Its softening point approaches 1700°C and can be used at 1000°C for a long time. It can work short-term at 1500°C. Silica fabric is applicable for use as a high temperature resistant, heat resistant, fire resistant,and corrosion resistant material.It is widely used in avaiation and aerospace, metallurgy, chemical, building material and fire fighting industry. Apart from applications requiring high temperature-resistance, it is also has insulation and fire prevention uses. Such as Thermal insulation covers, padding, lagging, welding blanket, fire curtain and other heavy duty fire control system. Silica cloth is suitable for coating with difference elastomers and polymers.
| Model No. | Thickness (mm) | Width (mm) | Weight (g/m2) | Weave | Roll length (meters) | Color |
| HS-026-P | 0.26 | 820 | 240g | Plain | 100 | White |
| HS-065-P | 0.65 | 860 | 590 | 50 | ||
| HS-076-P | 0.76 | 860 | 680 | 50 | ||
| HS-100-P | 1 | 860 | 915 | 50 | ||
| HS-135-P | 1.35 | 860 | 1250 | 50 | ||
| HS-065-T | 0.65 | 920 | 590 | Satin | 46 | White / Golden |
| HS-065-T | 0.65 | 1500 | 590 | 46 | ||
| HS-076-T | 0.76 | 920 | 680 | 46 | ||
| HS-100-T | 1 | 920 | 915 | 46 | ||
| HS-135-T | 1.35 | 920 | 1250 | 46 |
Advantages
1. Fire Resistant, heat resistance
2..Extremely high-temperature resistance up to 1500 C
3.Good anti-abrasion, easy to be cut, sewn and fabricated
4. Durability, High Strength, Corrosion Resistant
Main application
--Heat and flange shielding,insulation jackets,cover,mattress,pad
--Fire Doors,fire curtain,welding blankets,fire blankets
--Hose and cable protection
--- Protective garments
--Stress relief
--Gasket, seal
-- Car
Silicone rubber coated silica fbaric is silica fabric coated one side or both sides with silicone rubber. The material has a higher strength base fabric and higher temperature capability compared to conventional welding fabric, making it suitable for heavy-duty protection of personnel and equipment. Moreover, the coated material exhibits outstanding abrasion resistance.
Silicone Coated Silica Fabrics for industrial application requiring a compromise of thermal protection and abrasion resistance properties.| Item No. | Coating | Norminal Weight | Norminal Thickness | Weave Pattern | Standard Width(cm) | Base Fabric Tensile strength(N/INCH) | Fabric Yarn | Working Temperature(ºC) | |||
| gsm | osy | mm | warp | weft | fabric | coating | |||||
| SLS420 | 2 sides | 420 | 12.4 | 0.35 | Twill 3*1 | 92 | >300 | >250 | 96% silica | 1000 | 260-280 |
| SLS500 | 2 sides | 500 | 14.7 | 0.4 | Twill 3*1 | 92 | >300 | >250 | 96% silica | 1000 | 260-280 |
| SLS760 | 2 sides | 760 | 22.4 | 0.75 | Satin 8HS | 92/100/127 | >600 | >500 | 96% silica | 1000 | 260-280 |
| SLS810 | 2 sides | 810 | 23.9 | 0.75 | Satin 8HS | 92/100/127 | >600 | >500 | 96% silica | 1000 | 260-280 |
| SLS870 | 2 sides | 870 | 25.7 | 0.8 | Satin 8HS | 92/100/127 | >600 | >500 | 96% silica | 1000 | 260-280 |
Polyurethane (PU) coated Silica Fabric is made of fiberglass which is woven by high quality high silica filament yarns, and then coated with Polyurethane (PU) on single side or both sides, finally colored with aluminum pigments.
| Item No. | Coating | Norminal Weight | Norminal Thickness | Weave Pattern | Standard Width(cm) | Base Fabric Tensile strength(N/INCH) | Fabric Yarn | Working Temperature(ºC) | |||
| gsm | osy | mm | warp | weft | fabric | coating | |||||
| SLP420 | 2 sides | 430 | 12.7 | 0.41 | Satin 4HS | 92 | >300 | >250 | 96% silica | 1000 | 260-280 |
| SLP630 | 2 sides | 630 | 18.6 | 0.63 | Satin 8HS | 92/100 | >500 | >350 | 96% silica | 1000 | 260-280 |
Properties:
PU coated fiberglass fabric features good rebound resilience, toughness, softness,good abrasion & allergen resistance, oils resistance, cold,aging and weather resistance,and anti-solvents, and water proof.it can withstand temperature up to 180ºC for short bursts,this kind of cloth has lots of positive properties,bright in color, It also has the function of an anti bacterium,and can also be used for mould proofing, heat-insulation and anti-ultraviolet.
Inspection item | Technical index | ||||
Weight | 460g/m2 | 620g/m2 | 690g/m2 | 690g/m2 | 1070g/m2 |
Thickness | 0.4mm | 0.77mm | 0.63mm | 0.7mm | 1.2mm |
Temperature resistance | -50ºC~180ºC | ||||
Color | Green,Silver | ||||
Fabric style | Fiberglass with steel reinforced,Fiberglass | ||||
Fire resistance | Non-flammable(NF92507,M0) | ||||
Applications | Insulation jackets,mattress and Pad,fabric expansion joints,fabric ductwork connector,fire doors&fire curtains,welding/fire blankets. | ||||
Inspection item | Technical index | |||||
Weight | 220g/m2 | 460g/m2 | 640g/m2 | 720g/m2 | 720g/m2 | 880g/m2 |
Thickness | 0.21mm | 0.4mm | 0.86mm | 0.7mm | 0.72mm | 0.9mm |
Temperature resistance | -50ºC~180ºC | |||||
Color | Red/white color,yellow/green color,grey/white color,blue/black color,silver grey color,white,red,black,yellow,blue,green,silver grey | |||||
Fabric style | Fiberglass with steel reinforced,fiberglass | |||||
Fire resistance | Non-flammable(NF92507,M0) | |||||
Applications | Insulation jackets,mattress and Pad,fabric expansion joints,fabric ductwork connector,fire doors&fire curtains,welding/fire blankets | |||||
Storage
Unless otherwise specified, the fiberglass products should be in dry, cool and moisture-proof area. The room temperature and humidity should be always maintained at 15ºC~35ºC and 35%~65%. It is best if the price is used within 12 months after production date. The fiberglass products should remain in their original packaging until just prior to user.