QINGDAO FUTURE CHEMISTRY CO.,LTD
CERTIFICATE OF ANALYSIS
| Items | ASA | TYPE | COLOR PARTICLE | | TEST DATE | 2023-2-06 | MACHINE12 |
| | TEST ITEM | TEST STANDARD | TEST CONDITION | UNIT SI | SPECIFICATION | RESULT | INSPECTOR |
| |
PARTICLE APPEARANCE | UNIFORM SIZE,SMOOTH SURFACE INTEGRITY STRUCTURAL INTEGRITY, COLOUR UNIFORMITY. | | | | | |
| | DENSITY | GB/T 1033.1 | WT ºC | g/cm3 | | 1.077 | |
| | IZOD IMPACT TEST | GB/T1843 | 2mm NOTCHED, BREAK,CHARPY IMPACT J | J/m | | 352 | |
| | IZOD IMPACT TEST (LT) | GB/T1843 | 2mm NOTCHED,BREAK,CHARPY J,LT ºC, h | J/m | | | |
| | TENSILE STRENGTH | GB/T1040 | 50mm/min | MPa | | 45.6 | |
| | ELONGATION AT BREAK | GB/T1040 | 50mm/min | % | | 20.4 | |
| | BENDING STRENGTH | GB/T9341 | 2mm/min | MPa | | 66.7 | |
| | FLEXURAL MODULUS | GB/T9341 | 2mm/min | MPa | | 2172 | |
| | MELT FLOW RATE | GB/T 3682 | 220 ºC, 10 KG | g/10min | | 19.8 | |
| | MOISTURE CONTENT | GB/T2914 | ºC | % | | | |
| | FLAME RETARDANCE | GB/T2408 | V | | | | |
| | MOLD SHRINKAGE | GB/T 17037.4 | MD/TD | ºC | | | |
| | HEAT DISTORTION TEMP | GB/T 1634 | MPa | ºC | | | |
| | VICAT SOFTENING TENPERATURE | GB/T 1633 | N | ºC | | 85 | |
| | BALL INDENTATION HARDNESS | GB/T 3398 | | N/mm2 | | | |
| | SHORE HARDNESS | GB/T 2411 | | A D | | 103 | |
| | ODOR | PV3900 | | | | | |
| | TEST ENVIRONMENT | GB/T 2918 | | | | | |
1. Good compatibility with resin and good dispersion performance
2. Suitable for Molding, Extrusion,Blow Molding Processing Technology
3. Low Migration, No Color Dirty
4. High weather resistance
The Packing is 25kg/ bag, Paper-plastic compound bag outer, please store in the dry place.
We produce production of high performance and price ratio of modified engineering plastics,ASA film,ASA co-extrusion material,PMMA color co-extrusion material, Color masterbatches,PP,ABS,AS,PC,PE,PA, tarpaulin masterbatch, flame retardant masterbatches, antistatic masterbatches, anti-ultraviolet masterbatches and stabilizers, etc
Complaint