Structural PVC Foam China Professional Environmental PVC Foam for Sandwich Panel
PVC foam, with unique closed cell and cross linked structure, has good properties of high stiffness, strength to weight ratio, superior toughness, low water absorption and excellent resistance to chemicals. the fine cell structure gives a good bonding surface. It is compatible with unsaturated polyester resin, epoxy resin, vinyl ester resin etc, and widely used in the applications of wind energy, aerospace, marine, automobile, train, sports goods and so on.
We will suggest different types according to your application.
Strucell P passed GL certification,ABS certification,DNV certification,DIN551,NFF16-101,ROHS,SGS.
Feature:
density:60 - 200 kg/m3
good performance in hardness
Excellent anti-fatigue resistance, good impact resistance, low suction rate, thermal insulation
Good flame retardant performance
It is not easy to be damp and mildew
Good dimensional stability and processability, suitable for the manufacturing process of various sandwich structures, and compatible with a variety of resin systems, is the ideal core of the lightweight composite sandwich structure
processing temperature-240ºC~+100ºC,Use temperature-240ºC~+80ºC
| Item | Unit | P48 | P60 | P80 | P100 | P130 | P200 | P250 |
| Density | Kg/m3 | 48 | 60 | 80 | 100 | 130 | 200 | 250 |
| Density(Nominal) | Kg/m3 | / | 54 | 72 | / | / | / | / |
| Tensile strength | Mpa | 1.4 | 1.8 | 2.5 | 3.5 | 4.5 | 7.1 | 9.2 |
| Tensile strength | Mpa | 1.1 | 1.5 | 2.2 | 2.5 | 3.5 | 6.3 | 8 |
| Tensile modulus | Mpa | 55 | 75 | 95 | 130 | 175 | 250 | 360 |
| Tensile modulus | Mpa | 45 | 57 | 85 | 105 | 135 | 210 | 320 |
| Compressive strength | Mpa | 0.6 | 0.93 | 1.4 | 2 | 3 | 4.8 | 6.2 |
| Compressive strength | Mpa | 0.5 | 0.7 | 1.15 | 1.65 | 2.4 | 4.2 | 5.4 |
| Compressive modulus | Mpa | 50 | 70 | 90 | 135 | 170 | 240 | 300 |
| Compressive modulus | Mpa | 45 | 60 | 80 | 115 | 145 | 200 | 240 |
| Shear strength | Mpa | 0.5 | 0.76 | 1.15 | 1.44 | 2.1 | 3.5 | 4 |
| Shear strength | Mpa | 0.46 | 0.63 | 0.95 | 1.4 | 1.9 | 3.2 | 3.9 |
| Shear modulus | Mpa | 15 | 20 | 27 | 35 | 50 | 85 | 104 |
| Shear modulus | Mpa | 12 | 16 | 23 | 28 | 40 | 75 | 88 |
| Shear elongation,at break | % | 8 | 10 | 15 | 15 | 20 | 20 | 20 |
| Shear elongation,at break | % | / | 20 | 30 | / | / | / | / |