Polyethylene terephthalate (PET), chemical formula (C10H8O4) N, is by dimethyl terephthalate and ethylene glycol ester exchange or to terephthalate and ethylene glycol esterification synthesis of dihydroxyethyl terephthalate, and then the condensation reaction. Is a crystalline saturated polyester, milky white or light yellow, highly crystalline polymer, smooth and shiny surface, is a common resin in life, can be divided into APET, RPET and PETG.
In a wide temperature range with excellent physical and mechanical properties, long-term use temperature up to 120ºC, excellent electrical insulation, even at high temperature and high frequency, its electrical properties are still good, but the corona resistance is poor, creep resistance, fatigue resistance, friction resistance, dimensional stability is very good.
2.Application
Tube, Headdress, Elastic, Straps, Rope skipping, Air-Cushion etc
Properties | condition | unit | value |
Specific Gravity | 23ºC | g/cm3 | 1.19 |
Tensile Strength | 50mm/min | Mpa | 40 |
Elongation at Break | 50mm/min | % | 500 |
Tear Strength | 3mm/min | Kn/m | 110 |
Shore A | 23ºC | A | 85 |
ITEM | Value | Unit | Standard |
Density | 0.938 | g/cm3 | ASTM D1505 |
Melt Index 2.16kg | 2.5 | g/10 min | ASTM D1238 |
VA Content | 18 | Wt% | |
Shore Hardness A | 88 | ASTM D2240 | |
Shore Hardness D | 38 | ASTM D2240 | |
Tensile strength Yield | 4.41 | MPa | ASTM D638 |
Tensile strength Break | 14.7 | MPa | ASTM D638 |
Elongation Break | 800 | % | ASTM D638 |
Melting temperature | 84 | ºC | |
Vicat Softening Temperature | 60 | ºC | ASTM D1525 |
Low Temperature Brittleness | -70 | ºC | ASTM D746 |