ROAD® HDPE Geomembrane is manufactured from High Density Polyethylene resins by the technology of coextrusion-blown triple layer.The surfaces of both sides are smooth.
Properties | Test Method | GMSH050 | GMSH075 | GMSH100 | GMSH150 | GMSH200 |
Thickness | ASTM D5199 | 0.50 mm | 0.75 mm | 1.00 mm | 1.50 mm | 2.00 mm |
Density | ASTM D1505 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc |
Tensile Properties | ||||||
Yield strength Break strength Yield elongation Break elongation | ASTM D6693 Type IV | 7 kN/m 13 kN/m 12% 700% | 11 kN/m 20 kN/m 12% 700% | 15 kN/m 27 kN/m 12% 700% | 22 kN/m 40 kN/m 12% 700% | 29 kN/m 53 kN/m 12% 700% |
Tear Resistance | ASTM D1004 | 62 N | 93 N | 125 N | 187 N | 249 N |
Puncture Resistance | ASTM D4833 | 160 N | 240 N | 320 N | 480 N | 640 N |
Stress Crack Resistance | ASTM D5397 | 500 hrs | 500 hrs | 500 hrs | 500 hrs | 500 hrs |
Carbon Black Content | ASTM D1603 | 2.0% | 2.0% | 2.0% | 2.0% | 2.0% |
Carbon Black Dispersion | ASTM D5596 | For 10 different views:9 in Categories 1 or 2 and 1 in Category 3 | ||||
Oxidative Induction Time (OIT) | ASTM D3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. |
UV Resistance High Pressure OIT retained after 1600hrs | ASTM D5885 | 50% | 50% | 50% | 50% | 50% |
Dimensions | ||||||
Roll Width (m) | 7 | 7 | 7 | 7 | 7 | |
Roll Length (m) | 420 | 280 | 210 | 140 | 105 |