Description
Artificial marble, polyester concrete resin
Artificial marble resin is widely used in the production of products such as kitchen countertops, toilet wash-face dressing tables and bathtubs. It has a complete variety and has its own characteristics. Polyester concrete resin is suitable for the production of cellar covers, fire hydrants and other products. The products have high compressive strength and service life. long feature
Quartz Stone, Marble, Polyester Concrete Resin
UPR for cultured marble is used for the casting of cultured marble, tabletop, bath tub, etc. UPR for Polymer concrete is used for products manhole covers and hydrant.A: RC NX-37 Unsaturated Polyester Resin
1.Features and usage:
RC NX-37 is used to produce translucent, good three-dimensional artificial marble/agate products.It has light color, low shrinkage, air-drying, weather resistance, and good hot water resistance. It is suitable for medium temperature production to make high-end bathroom facilities. 2.Technical index of liquid resin (25 ºC):
Item | Unit | Index | Testing method |
Appearance | --- | Light yellow transparent liquid | B80101 |
Hazen | --- | ≤50 | B42300 |
Viscosity | Pa•s | 0.50~0.60 | B54953 |
Gel time | min | 3.7~4.7 | C82012 |
Proportion | --- | 1.065~1.085 | JIS K 6901.4.1.2 |
Note: Gel time test: resin 50g; accelerator RP-153 1.0%; curing agent Butanox M-50 1.0% 3.Physical properties of casting body (for reference only)
Item | Unit | Index | Testing method |
Tensile Strength | MPa | 75.4 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 3090 |
Elongation at Break | --- | 4.02% |
Bending Strength | MPa | 118.0 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | MPa | 3310 |
Impact Strength | KJ/m2 | 18.0 | GB/T2567-2008 |
Heat Deflection Temperature | ºC | 109 | GB/T1634-2004 |
Bacol hardness | --- | 42 | GB/T3854-2005 |
Relative Density | --- | 1.16 | GB/T1463-2005 |
Note: 1.the sample method of casting system:GB / t8237-2005, curing system: accelerator rp-153: 1.0%; Curing agent butanox m-50:1%
2.Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 120 ºC × Two hours.
4.Instructions:
RC nx-37 resin 100 units
Medium temperature curing agent 0.3 ~ 0.7
Al(OH)3 200 units 5.Notices:
The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory. 6.Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
B: RC TP-156 Unsaturated Polyester Resin
1.Features and usage:
RC TP-156 is used to produce translucent, three-dimensional artificial marble/agate products (eg: washing and dressing table, kitchen countertop, bathtub). It is a kind of pre-accelerated resin with air-drying character, can be colored vividly with a small amount of pigment; excellent curability, short molding cycle, light cured material, high heat distortion temperature, small product warpage, UV stability and good stain resistance. 2.Technical index of liquid resin (25 ºC):
Item | Unit | Index | Testing method |
Appearance | --- | Light violet liquid | B80101 |
Viscosity | Pa•s | 1.30~1.70 | B54953 |
Gel time | min | 10.0~16.0 | C82801 |
Note: Gel time test: resin 50g; curing agent Butanox M-50 1.0% 3.Physical properties of casting body (for reference only)
Item | Unit | Factual Value | Testing Method |
Casting body | Marble |
Tensile Strength | MPa | 66 | 33.1 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 4060 | 12300 |
Elongation at Break | --- | 1.7% | 0.30% |
Bending Strength | MPa | 108 | 49.3 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | MPa | 3900 | 10600 |
Impact Strength | KJ/m2 | 7 | 2.55 | GB/T2567-2008 |
Heat Deflection Temperature | ºC | 90 | 130 | GB/T1634-2004 |
Bacol hardness | --- | 47 | 62 | GB/T3854-2005 |
Water-absorbing(25ºC,24h) | --- | 0.3% | 0.029% | GB/T1462-2005 |
Note:
1) The casting system sample method: GB/T8237-2005, and the curing system: Huangyan MEKP 1.0%;
2) Post-curing treatment of casting body: room temperature×24 hours+60ºC×3 hours+110ºC×2 hours;
3) Marble post-curing treatment: room temperature × 24 hours + 60° C. × 1 hour + 80° C. × 2 hours + 130° C. × 2 hours. 4.Instructions:
RC TP-156 resin 100 units
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 200 units 5.Notices:
The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory. 6.Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
C: RC TP-254 Unsaturated Polyester Resin
1.Features and usage:
RC TP-254 is an isophthalic acid type unsaturated polyester resin, used to produce rigid, heat-resistant artificial marble (bathtubs, wash basins). Combined with a low shrinkage agent, it has excellent low shrinkage and can be quickly formed at high temperature. 2.Technical index of liquid resin (25 ºC):
Item | Unit | Index | Testing method |
Appearance | --- | Light yellow transparent liquid | JIS K 6919.5.1.3 |
Gardner | --- | ≤3 | JIS K 6901.5.2 |
Viscosity | Pa•s | 0.42~0.52 | JIS K 6901.5.5.1 |
Gel time | min | 4.2~7.8 | JIS K 6901.5.10 |
Note: Gel time test: resin 50g; accelerator RC 2.0%; curing agent Butanox M-50 2.0% 3.Physical properties of casting body and marble (for reference only):
Item | Unit | Factual Value | Testing Method |
Casting body | Marble |
Tensile Strength | MPa | 62.8 | 28.2 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 3500 | 10200 |
Elongation at Break | --- | 2.15% | 0.31% |
Bending Strength | MPa | 102 | 53.9 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | MPa | 3240 | 9310 |
Impact Strength | KJ/m2 | 11.4 | 2.98 | GB/T2567-2008 |
Heat Deflection Temperature | ºC | 128 | >140 | GB/T1634-2004 |
Bacol hardness | --- | 42 | 60 | GB/T3854-2005 |
Hydroscopic Rate(25ºC,24h) | | 0.209% | --- | GB/T1462-2005 |
Note: 1.the casting system and sample method: GB / t8237-2005, and the curing system is rp-153 1.0%; The MEKP of Huangyan is 1.0%;
2. Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 120 ºC × 2 hours;
3).Post curing treatment of marble: room temperature × 24 hours + 60 ºC × 1 hour + 80 ºC × 2 hours + 130 ºC × Two hours. 4.Instructions:
RC TP-254 Resin 100 units
Accelerator RC-153 1.0
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 200 units 5.Notices:
1.When the construction environment temperature is high and the gel time is short, the amount of curing agent cannot be reduced, and the gel retarder RC-406 should be added as needed.
2.The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory. 6.Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
D: RC-H-1036L Unsaturated Polyester Resin
1.Features and usage:
RC-H-1036L unsaturated polyester resin is used to produce artificial marble countertops and sanitary ware. It has good water resistance, crack resistance and pollution resistance. Used in conjunction with colorless accelerator RP-153, the cured product has a light color and low exothermic peak. 2.Technical index of liquid resin (25 ºC):
Item | Unit | Index | Testing method |
Appearance | --- | Light yellow transparent liquid | B80101 |
Hazen | --- | ≤80 | B42300 |
Viscosity | Pa•s | 0.60~0.80 | B54953 |
Gel time | min | 10.0~18.0(from May to October) | HR-1040 |
6.0~10.0(November to next April) |
Non-volatile material | % | 64.0~68.0 | B22301 |
Note: Gel time test: resin 50g; accelerator RCA: 1.5%; curing agent Butanox M-50: 1.0%. 3.Physical properties of casting body and marble (for reference only):
Item | Unit | Factual Value | Testing Method |
Casting body | Marble |
Tensile Strength | MPa | 69.2 | 22.4 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 3760 | 11300 |
Elongation at Break | --- | 2.48% | 0.22% |
Bending Strength | MPa | 129 | 55.0 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | MPa | 3890 | 11300 |
Impact Strength | KJ/m2 | 11.7 | 3.23 | GB/T2567-2008 |
Heat Deflection Temperature | ºC | 65 | 90 | GB/T1634-2004 |
Bacol hardness | --- | 43 | 66 | GB/T3854-2005 |
Note:
1.The sample preparation method of casting system:GB / t8237-2005, and the curing system is rp-153 1%; Curing agent butanox m-50 1%; 2) Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 80 ºC × 2 hours;2.Post curing treatment of marble: room temperature × 24 hours + 60 ºC × 1 hour + 80 ºC × 2 hours + 100 ºC × Two hours.
4.Instructions:
RC-H-1036L Resin 100 units
Accelerator RC-153 1.0
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 200 units 5.Notices:
1.When the construction environment temperature is high and the gel time is short, the amount of curing agent cannot be reduced, and the gel retarder RC-406 should be added as needed.
2.The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory. 6.Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
E: RC TPH-3143 Unsaturated Polyester Resin
1.Features and usage:
RC TPH-3143 is a kind of pre-accelerated unsaturated polyester resin in bisphenol A type with high refractive index resin,low exothermic;also good corrosion resistance, used in conjunction with aluminum hydroxide, used to produce highly transparent, three-dimensional artificial marble/agate products (Example: Washing and dressing table, kitchen countertop); The product has small warpage and deformation. 2.Technical index of liquid resin (25 ºC):
Item | Unit | Index | Testing method |
Appearance | --- | Light violet green liquid | B80101 |
Viscosity | Pa•s | 1.00~1.30 | B54953 |
Gel time | min | 25.0~35.0 | JIS K 6901.5.10 |
Note: Gel time test: resin 50g; curing agent Butanox M-50 1.0% 3.Casting performance (for reference only)
Item | Unit | Index | Testing method |
Tensile Strength | MPa | 64.3 | GB/T2567-2008 |
Elastic Tensile Modulus | MPa | 3830 |
Elongation at Break | --- | 2.26% |
Bending Strength | MPa | 105 | GB/T2567-2008 |
Modulus of elasticity ( MOE) | MPa | 3940 |
Impact Strength | KJ/m2 | 10.6 | GB/T2567-2008 |
Heat Deflection Temperature | ºC | 67.8 | GB/T1634-2004 |
Bacol hardness | --- | 40 | GB/T3854-2005 |
Note:
1) The sample preparation method of casting:GB / t8237-2005, and the curing system is M50 1.0%;
2) Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 80 ºC × 2 hours;
3) marble post curing treatment: room temperature × 24 hours + 60 ºC × 1 hour + 80 ºC × 2 hours + 90 ºC × Two hours. 4.Instructions:
RC TPH-3143 resin 100 units
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 100 units 5.Notices:
1.When the construction environment temperature is high and the gel time is short, the amount of curing agent cannot be reduced, and the gel retarder RC-406 should be added as needed.
2.The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory. 6.Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.
Founded in 2002, Changzhou Rule Composite Material Co., Ltd, is a enterprise engaged in in manufacturing high-performance unsaturated polyester resin, gel coat, glass fiber reinforced composite materials and other related products, also professional in research, development as well as technical consulting and services of composite materials.
Rule Composite Material covers an area of 50, 000 square meters, with a modern office building, an independent R& D center and a high-standard production workshop, equipped with the leading DCS automatic control production device. We also have a strong and advanced quality control department and technical support laboratory.
RULE focuses on the production of excellent-quality and creative-design resin products, so it is trustworthy. Our sweat and wisdom witness the footprints of yesterday's struggle, passion and dream fulfill today's victory. Forging ahead to make innovation in market economy, pursuing value of "innovation, creativity, sharing" in practice, it harvests a stream of praises and honors.
Our Advantages
Why we choose Changzhou Rule Composite Material Co., Ltd?
What is resin?
Resin usually refers to products inclined to softening or melting after receiving heat. When softening, it shows a trend toward flowing under the influence of external forces. Under normal temperature, it is in solid, semi-solid state, and sometimes liquid organic polymer. Broadly speaking, any macromolecule compound that can be used as a raw material for plastic processing can be called resin.
What can resins do for you?
Resin products are widely used in sectors like railways, automobiles, wind power, shipbuilding, cooling towers, pipelines, coatings, electrical appliances, artificial stone, handicrafts, lighting tiles, sanitary ware, anti-corrosion engineering and so on. Rule has been granted certification of ISO9001: 2008 Quality Management System and ISO14001: 2004 Environmental Management System, and some products have won recognition of China Classification Society(CCS) and Food-Level Licenses of the Provincial Department of Health.
We are the professional resin solution provider.
With decades of experience in the R& D of resins, we can fully understand customers' needs and aspirations in the cooperation process and have presented countless solutions. Over the years, we work hard to optimize our products and make them attractive to end users.