Test Parameter | Unit | Result |
As Supplied Tested at 23ºC and 50% RH | ||
Specific Gravity | g/ml | 0.97±0.02 |
Flow (sag or slump) | mm | 0 |
Extrusion Rate Skin Time | ml/minute minute | 130 5~10 |
Tack-free Time | hour | ≤1.0 |
Curing time (5mm) | hour | ≤8 |
As Cured-after 21 days at 23ºC and 50% RH | ||
Durometer Hardness, Shore A | Points | 30 |
Movement Capability | % | ±25 |
Tensile/Modulus at 50% Elongation | Mpa | 0.32 |
Tensile/Modulus at 100% Elongation | Mpa | 0.38 |
Ultimate Tensile Strength Ultimate Elongation at Break | Mpa % | 0.45 300 |