Dipped polyester tire cord fabrics
Dipped polyester tire cord fabrics have the excellent characteristics of high strength, low elongation, high module and better dimensional stability etc. There are two types: Dipped STD Polyester Tire Cord Fabrics and Dipped HMLS Polyester Tire Cord Fabrics

Characteristics:
Dipped STD Polyester Tire Cord Fabrics
High Strength, low elongation, better module and dimensional stability.Which was made from standard high strength polyester industrial filaments.
Dipped HMLS Polyester Tire Cord Fabrics
High module, low shrinkage etc. Which was made from HMLS polyester industrial filaments. Use this fabrics to produce radial tires can improve its fatigue resistance and heat dissipation, to improve its high speed performance and service life, have high oil saving rate, better control stability, ride comfort etc,. During the vulcanization process of radial tires, high temperature curing can be used, which avoid inflation process after vulcanization, reduce the equipment investment, and improve production efficiency.

Applications:
Radial tires for car, light truck, rubber hose, V-belt and other rubber products.

Specification:
1100dex/2, 1100dex/3, 1440dtex/2, 1440dtex/3, 1670dtex/2, 1670dtex/3, 2200dtex/2, 2200dtex/3 etc.
Note: The above are general technical specifications, which can be adjusted according to customer' requirements.

Dipped nylon tire cord fabrics
Dipped nylon tire cord fabrics is the rubber skeleton material have the excellent characteristics of high strength, better fatigue resistance, better impact resistance and less hysteresis loss etc.
There are two types: Dipped nylon 6 Tire Cord Fabrics and Dipped nylon 66 Tire Cord Fabrics.

Characteristics
High strength;
better fatigue resistance;
better impact resistance;
less hysteresis loss

Applications:
Dipped nylon tire cord fabrics can be used as the carcass and breaker of bias tire , the cap ply of radial tire, It is especially for large and medium-sized truck tires, earth-mover tires, aircraft tires, off-road tires and other tires with harsh conditions of use.

Specification:
930dtex/2, 1400dtex/2, 1870dtex/2, 2100dtex/2, 1400dtex/3 etc.
Note: The above are general technical specifications, which can be adjusted according to customer' requirements.

Dipped Aramid Tire Cord Fabrics
Dipped aramid tire cord fabrics have perfect performance with high strength , high module, heat resistant, small deformation, micro hot air shrinkage, low creep, better fatigue resistance and chemical resistance etc.

Characteristics
Dipped Aramid Tire Cord Favrics are made from high performance fiber- aramid fiber material, which have the characteristics of few density, low elongation, high strength, high module, heat-resistant, corrosion resistance etc. If such fabrics were used into the production of tires, it can reduce the weight of tires, rolling resistance and fuel consumption, also, the waste radial tire recycling has become possible, and will have a wide range of social and economic benefits.

Applications
Dipped Aramid Tire Cord Fabrics can be used as reinforcement in any part of radial tires, such tires have characteristics of low weight, better fatigue resistance, high module and low shrinkage etc., which have prosperous prospect in tires application.

Specification
1100dtex/2, 1670dtex/2, 1670dtex/3 etc.
Note: The above are general technical specifications, which can be adjusted according to customer' requirements.

Specification:
Nylon 6 Dipped Tyre Cord Fabric Specification

Item			1870dtex/2 (1680D/2)	1400dtex/2 1260D/2	930dtex/2 840D/2	2100dtex/2 (1890d/2)	1170dtex/1 (1050D/1)	700dtex/1 (630D/1)	1870dtex/1 (1680D/1)	1400dtex/1 (1260D/1)	930dtex/1 (840D/1)
Breaking strength≥		N/end	279.30	215.60	137.20	313.60	90.00	50.00	137.00	107.00	70.00
Elongation at	88.2N	%	9.5±0.5	-	-	9.5±0.5	-	-	8.0±0.8	-	-
	66.6N		-	9.5±0.5	-	-	8.0±0.8	-	-	7.0±0.8	-
	44.1N		-	-	9.5±0.5	-	-	7.5±0.8	-	-	7.5±0.8
Adhesive strength≥		N/cm	166.60	147.00	117.60	176.40	65.00	43.00	83.00	69.00	54.00
Breaking strength difference≤		%	3.80	3.80	3.80	3.80	5.00	5.00	5.00	5.00	5.00
Breaking elongation difference≤			6.30	6.30	6.30	6.30	7.00	7.50	7.00	7.00	7.00
Dip pick up			4.5±1.0	4.5±1.0	4.5±1.0	4.5±1.00	4.2±0.8	4.2±1.00	4.2±1.00	4.2±1.00	4.2±1.00
Breaking elongation		%	23.0±2.0	23.0±2.0	22.0±2.0	23±2.0	20.0±2.0	19.0±2.0	20.0±2.0	20.0±2.0	20.0±2.0
Diameter		mm	0.78±0.03	0.65±0.03	0.55±0.03	0.78±0.03	-	0.23±0.03	0.5±0.03	0.43±0.03	0.32±0.03
Twist	Primary twist(Z)	Twist/m	320±15	370±15	460±15	320±15	TPM/m: 200±15	TPM/m: 260±15	160±10	190±10	210±15
Twist	Second twist(S)	Twist/m	320±15	370±15	460±15	320±15	TPM/m: 200±15	TPM/m: 260±15	160±10	190±10	210±15
Heat shrinkage ≤		%	6.00	6.00	6.00	4.00	4.50	4.00	4.00	4.00	4.00
Moisture ≤		%	1.00	1.00	1.00	1.00	0.80	0.80	0.80	0.80	0.80

Polyester Dipped Tire Cord Fabric STD Specification

NO.	ITEMS		UNITE	1000D/2	1300D/2	1000D/3	1500D/2	2000D/2	1300D/3	1500D/3
NO.	ITEMS		UNITE	(1100dtex/2)	(1440dtex/2)	(1100dtex/3)	(1670dtex/2)	(2200dtex/2)	(1440dtex/3)	(1670dtex/3)
1	Breaking Stength (min)		N/end	140	180	205	205	280	260	305
2	Elongation at 44.1N		%	4.5+1.0
	Elongation at 58.0N		%		4.5+1.0
	Elongation at 66.6N		%			4.5+1.0	4.5+1.0
	Elongation at 88.2N		%					4.5+1.0	4.5+1.0
	Elongation at 100N		%							4.5+1.0
3	Adhension(H-test)(min)		N/Cm	125	135	140	140	170	165	180
4	Breaking strength difference(max)		%	4	4	4	4	4	4	4
5	Breaking elongation difference(max)		%	5	5	5	5	5	5	5
6	Dip pick up		%	3.5+1	3.5+1	3.5+1	3.5+1	3.5+1	3.5+1	3.5+1
7	Breaking elongation (Min.)		%	15+/-2	15+/-2	15+/-2	15+/-2	15+/-2	15+/-2	15+/-2
8	Diameter		mm	0.56+0.03	0.61+0.03	0.66+0.03	0.66+0.03	0.75+0.03	0.74+0.03	0.81+0.03
9	Twist	Pingle twist(Z)	T/10cm	45+1.5	40+1.5	37+1.5	37+1.5	33+1.5	33+1.5	31+1.5
9	Twist	Ply twist(S)	T/10cm	45+1.5	40+1.5	37+1.5	37+1.5	33+1.5	33+1.5	31+1.5
10	Hot air shrinkage 177ºC×2minx0.05CN/dtex(max)		%	3	3	3	3	3	3	3
11	Elongation @ Breaking of weft yarn (Min)		%	120	120	120	120	120	120	120

Polyester Dipped Tyre Cord Fabric HMLS Specification

NO.	ITEMS		UNITE	1000D/2	1300D/2	1000D/3	1500D/2	2000D/2	1300D/3	1500D/3
NO.	ITEMS		UNITE	(1100dtex/2)	(1440dtex/2)	(1100dtex/3)	(1670dtex/2)	(2200dtex/2)	(1440dtex/3)	(1670dtex/3)
1	Breaking Stength (min)		N/end	140	180	205	205	270	260	305
2	Elongation at 44.1N		%	4.5+1.0
	Elongation at 58.0N				4.5+1.0
	Elongation at 66.6N					4.5+1.0	4.5+1.0
	Elongation at 88.2N		%					4.5+1.0	4.5+1.0
	Elongation at 100N		%							4.5+1.0
3	Adhension(H-test)(min)		N/Cm	125	135	140	140	170	165	180
4	Breaking strength difference(max)		%	4	4	4	4	4	4	4
5	Breaking elongation difference(max)		%	5	5	5	5	5	5	5
6	Dip pick up		%	3.5+1	3.5+1	3.5+1	3.5+1	3.5+1	3.5+1	3.5+1
7	Breaking elongation (min)		%	14	14	14	14	14	14	14
8	Diameter		mm	0.56+0.03	0.61+0.03	0.66+0.03	0.66+0.03	0.75+0.03	0.74+0.03	0.81+0.03
9	Twist	Pingle twist(Z)	T/10cm	45+1.5	40+1.5	37+1.5	37+1.5	33+1.5	33+1.5	30+1.5
9	Twist	Ply twist(S)	T/10cm	45+1.5	40+1.5	37+1.5	37+1.5	33+1.5	33+1.5	30+1.5
10	Hot air shrinkage 177ºC×2minx0.05CN/dtex(max)		%	2	2	2	2	2	2	2
11	Elongation @ Breaking of weft yarn (Min)		%	120	120	120	120	120	120	120

Product pictures:

Why choose us?
1.A professional international sales team, which is specialized in the framework materials for 16 years.
2.Well and high-quality control
3. Strong production capacity and testing capabilities
4.Various designs are available
5.Prompt delivery
6.FREE SAMPLE can be offered

Forward

Related products