Stainless Steel Welding Electrodes Aws E308L-16 Welding Rod

Min.Order: 1,000

Product origin: Wenzhou, Zhejiang, China

Infringement complaint:

Complaint

US$ 2.8 ~ 3.5

Description

Product Description

E308L-16 Stainless Steel Welding Electrode/Rod

Description:

A002 is a super-low carbon Cr19Ni10 stainless steel type electrode coated with Titanium-calcium.The molten content is ≤0.04%.It provides excellent performance of intorcry stalline corrosion resistance.It has excellent operational technological performace on both AC and DC.

Application:

It applies to welding the structure of super-low carbon Cr19Ni10 stainless steel.It also suitable for welding the structure of anti-corrosion stainess steel 0Cr19NillT1 which working temperature below 300ºC.It is mainly used for equipment manufacturing of fibre,fertilizer and petroleum industry.

Chemical Composition Deposited Metal (%)
C	Mn	Si	Cr	Ni	S	P	Mo	Cu
≤0.04	0.5~2.5	≤0.90	≤18~21	9~11	≤0.03	≤0.04	≤0.75	≤0.75

Mechanical Properties of Deposited metal
Test Item	Tensile Strength ós (Mpa)	Elongation δ5(%)

Guranteed	≥520	≥35

Sizes & Recommended Current (AC or DC)
Welding rod diameter (mm)	2.0	2.5	3.2	4.0	5.0
welding current (A)	25~50	50~80	80~110	110~160	160~200

Notes:

1.Electrodes must be baked for 1 hour at 150ºC before welding operation.
2.To operate on DC if all possible.Operate with small current so the electrode will not in red-hot.
3.The anti-corrosion performance and ferrite composition should be detemined between buyer and seller

-------------------Our Other Welding Products-------------------
If you are interested, please click on the below picture to enter the link

Welding Electrode Carbon Steel, Stainless Steel, Cast Iron etc.	Nickel & Cobalt Based Hardfacing Welding Consumbale	Flux Cored Welding Wire E71T-1,E71T-1C, E71T-GS,E81T-Ni etc.

TIG & MIG Aluminum Welding Wire ER5356,ER4043, ER4047, ER5183 etc.	Submerged Arc Welding Wire EM12,EM12K,EL12,EH14 etc.	Co2 MIG Welding Wire ER70S-6(SG2),SG3 etc.