Complaint
Product Introduction
Alumina Zirconia Ceramic Ball are made of alumina and zirconia after rolling forming and then calcined at high temperature. The composition of zirconia in the composite zirconia beads increases the toughness of the composite zirconia beads, and the spherical surface is smooth, so the abrasion is lower than that of alumina balls, which has less wear on the grinding machine and reduces power consumption. Composite zirconium beads are suitable for grinding materials with high hardness.
Advantages
a. Compared with zirconium-containing grinding media, the one-time investment is less;
b. Compared with the general high aluminum ball, the density is higher, and the grinding efficiency is high;
c. Compared with high-aluminum balls at the same price, the wear is lower, and the cost performance is high;
d. High hardness, high strength and low crushing rate;
e. The size is relatively complete, which can be applied to different industries and different equipment requirements.
Product Application
Alumina Zirconia Ceramic Ball mainly used in non-ferrous metal ores, industrial ceramic powder materials, non-metallic powder materials, titanium dioxide, papermaking, coatings, inks, other powder materials, etc. Grinding medium of various equipment such as machine and sanding machine.
Technical Data
| Series | BMZTA10 | BMZTA15 | BMZTA60 | BMZTA70 |
| ZrO2 (%) | 10±0.5 | 15±0.5 | 60±0.5 | 70±0.5 |
| Hardness(Mohs) | 7 | 8 | 8 | 8 |
| Bulk density(g/cm3) | ≥3.2 | ≥3.8 | ≥4.5 | ≥4.7 |
| Self wearing rate(‰) | ≤0.02 | ≤0.015 | ≤0.01 | ≤0.008 |
| Dimension(mm) | φ1-10 | φ1-10 | φ1-10 | φ1-10 |