Complaint
| Properties | ISO Test Method | Test Condition | Unit | CM-205 |
| Melt Flow Index | 1133 | 230ºC×3.8KG | ml/10 min | 1.9 |
| Mass Density | 1183 | 23 ºC | g/cm3 | 1.19 |
| Tensile Strength | 527 | 5 mm/min, yield | MPa | 70 |
| 5 mm/min, break | MPa | 70 | ||
| Tensile Elongation | 527 | 50 mm/min | % | 12 |
| Flexural Strength | 178 | 2 mm/min | MPa | 103 |
| Flexural Modulus | 2 mm/min | GPa | 2.8 | |
| Izod Impact Strength | 180/1A | 23 ºC Notched | KJ/m2 | 2 |
| -30 ºC Notched | KJ/m2 | - | ||
| Charpy Impact Strength | 179 | 23 ºC Notched | KJ/m2 | 2 |
| -30 ºC Notched | KJ/m2 | - | ||
| Vicat Softening Temp. | 306 | 1 Kg,50 ºC/hr | ºC | 115 |
| 5 Kg,50 ºC/hr | ºC | 107 | ||
| Heat Distortion Temp. | 75/A | 1.8 MPa Unannealed | ºC | 95 |
| 1.8 MPa Annealed | ºC | 104 | ||
| Coefficient of Linear Thermal Expansion | 11359 | - | - | 6 X 10-5 |
| Flammability | - | UL-94 | - | 1.5mm HB |
| Mold Shrinkage | 294-4 | - | % | 0.2~0.6 |
| Symbol | 1043 | - | - | >PMMA< |
Molding methods include casting, injection molding, machining, thermoforming and so on. Especially injection molding, can be mass-produced, simple process, low cost. Therefore, its application is increasingly extensive, it is widely used in instrumentation parts, automotive lights, optical lenses, transparent pipes.
25kg/ carton or 25kg/bag, or per your requirement