Magnetic Polyurethane Ceramic Wear Liners
Rubber ceramic wear liners made of hexagonal ceramic tiles.
Metal and studs back rubber ceramic wear liners
Ceramic tile on rubber sheets, 500x500x8mm, 4mm ceramic on 4mm rubber ceramic mats. Can be produced with cn layer.
Specifications of rubber ceramic wear liners
Item | Description | Unit | Result |
Alumina Ceramic | |||
1 | Alumina(Al2O3) | % | 92, 95 |
2 | Density | g/cm3 | 3.64 |
3 | Water Absorption | % | ≤0.01 |
4 | Hardness | Mohs | 9 |
Rubber | |||
1 | Material |
| NR or SBR |
2 | Gravity | g/cm3 | 1.15 |
3 | Tensile Strength | MPa | 15 min. |
4 | Hardness | Shore A | 55±5 |
5 | Elongation | % | 400 min. |
6 | Abrasion Loss | mm3 | ≤90 |
7 | Aging Coefficient (70C°x 48h) | % | 8.7 |
Application:
Ceramic wear liners offer excellent abrasion resistance, are ideal solutions for areas suffering severe wear and impact.
92% or 95% high alumina ceramic tiles exhibits excellent wear resistance.
Alumina ceramic wear liners are mainly used in the following applications:
Selection Chart for Rubber Ceramic Wear Liners:
Size (mm) | Thickness of ceramic (mm) | Thickness of rubber (mm) | Thickness of steel backing plate | Total thickness (mm) |
300x300x36 | Φ21x21 | 9 | 6 | 36 |
300x300x50 | Φ31x31 | 13 | 6 | 50 |
250x250x36 | Φ21x21 | 9 | 6 | 36 |
250x250x50 | Φ31x31 | 13 | 6 | 50 |
250x250x18 | 17.5x17.5x8 | 5 | 6 | 19 |
Abrasion resistant ceramic wear liners with steel plate and studs:
Ceramic rubber liners package:
Standard export packing, plywood pallet, no wood, no need fumigation
Pallet size: 1000*1000*620mm, Pallet weight: 1.2 tons
Pallet quantity for each 20GP container: 20~24 pallets
About Our Company:
Employee: 99
Floor area: 22,400 m2
Building area: 33,330 m2
Certificate:
√SGS audited supplier
√ISO9001 certified factory
√ISO14001 certified factory
√ISO45001 certified factory
√Safety Certificate of Approval for Mining Products
Further information, just contact Ms Mona Cheung.