Complaint
| Material | Lucite Acrylic |
| Thickness | 20-300mm customized |
| Color | Clear/transparent |
| Shape | Customer's Demand |
| Surface | High Surface Hardness |
| Light transmission | High light transmission(95%) |
| Diaphaneity | More than 93% |
| Packing | PE film masking on both sides,KT board and angle iron. |
| Application | undersea world, Oceanarium, Zoo, Luxurious hotels, Swimming pools and so on. |
| PROPERTIES | VALUES | RULES |
| Density | 1.19 g/cm3 | ISO 1183-1:2012 Method A |
| Rockwell Hardness | 112L | ISO 2039-2:1999 |
| Tensile Modulus | 3150MPa | EN ISO 527:2012 |
| Tensile Strength | 80.0MPa | EN ISO 527:2012 |
| Tensile Strain at Break | 3.2% | EN ISO 527-1:2012 |
| Water Absorption | 0.20% | ISO 62:2008 Method 1 |
| Total Luminous Transmittance | 93.4% | ISO 13468-1:1996 |
| Vicat Softening Temperature | 105ºC | ISO 306:2013 Method B50 |
| Light Ageing Test- UV Exposure | Grey scale: 5 | ISO 4892-3:2016 Cycle 1 |
| Mean Coefficient of Linear Thermal Expansion | 72×10-6 K-1 | ISO 11359-1:2014 |
| Compressive Stress at Yield | 129MPa | EN ISO 604:2003 |
| Flexural Strength | 120MPa | ISO 178:2013 |
| Compressive Yield Strength | 111MPa | ASTM D695-15 |
| Compressive Modulus | 3450MPa | ASTM D695-15 |
| Shear Strength | 59.7MPa | ASTM D732-17 |
| Deflection Temperature under Load | 100.2ºC | ASTM D648-18 Method B |
| Modulus Elasticity | 2810MPa | ASTM D695-15 |