Polyvinyl Chloride Chinapvc Resin 25kg Bag PVC Resin S1000 S700 S1300 Sinopec

Min.Order: 1

Product origin: Shijiazhuang, Hebei, China

Infringement complaint:

Complaint

US$ 650 ~ 850

Description

Polyvinyl chlorides is high molecular compounds polymerized with structural element as CH2-CHCLn,degree of polymerization usually as 590-1500.In the process of re-polymerization ,affected by kinds of factors such as the polymerization process, reaction conditions, reactant composition, additives etc.it can produce eight different types of PVC resin performance is different.

Product Name	Polyvinyl Chlorides Resin S700 S1000
Brand Name	Sinopec
Appearance	White stable powder
Particle size	60-250um
Apparent Density	0.4-0.6g/ml
Physical and chemical properties	100ml cyclohexanones contains 0.5g resin in dilute solution viscosity 80-160ml/ g, 100g resin absorbs 20-30 grams of plasticizer at room temperature.
Main use	It can be used to produce soft films, artificial leather, sheets, pipes, profiles, corrugated pipes, cable protection tubes,packaging films, hoses, shoe soles and various soft sundries.

PVC RESIN S-700
Grade		Measured Value
Specification		STANDARD	RESULT
Item
Appreance		White powder	White powder
Impurity Particle Number		≤16	10
Mass fraction of Volatile Matter (including water),%		≤0.3	0.14
Apparent Density,g/mL,≥		0.54-0.62	0.61
Reduce on Sieve,%	250umSieve Mesh ≤Sieve,	1.6	0
	63umSieve Mesh ≥Sieve,	97	97
"Fish Eye"/400cm²≤		≤16	7
100g Resin Plasticizer Absorption,g		≥14	16.4
Whiteness(160ºC,10min),%≥		≥75	70
Average degree of polymerization		650-750	700
Residual Vinyl Chlorides Monomer Content,ug/g		≤3	1

PVC RESIN S-1000
Grade		Measured Value
Specification		STANDARD	RESULT
Item
Appreance		White powder	White powder
Impurity Particle Number		≤16	10
Mass fraction of Volatile Matter (including water),%		≤0.3	0.14
Apparent Density,g/mL,≥		0.5-0.58	0.54
Reduce on Sieve,%	250umSieve Mesh ≤Sieve,	1.6	0
	63umSieve Mesh ≥Sieve,	97	98
"Fish Eye"/400cm²		≤12	6
100g Resin Plasticizer Absorption,g		≥20	24.8
Whiteness(160ºC,10min),%≥		≥78	84.7
Average degree of polymerization		970-1070	1010
Residual Vinyl Chlorides Monomer Content,ug/g		≤3	0.1