Sample | @40ºC Appearance | Density (g/cm3 @25oC) | Viscosity (mPa·s @40oC) | Package Size (kg/drum) |
HD-8090-1(POL, A, poliol) | Cream Liquid | 1.13~1.18 | 1800~2500 | 18 / 220 |
HD-2400(ISO, B) | Liquid | 1.18~1.20 | 50~250 | 20 / 235 |
HD-8090-1 | Hardener/g | water/g | catalyst/g | Post-catalyst | Otros aditivos |
18 kg(one drum/ un envase) | 400 | 90 | 300 | 100 | It depends |
220 kg (one drum/ un envase) | 4900 | 1100 | 3700 | 1200 | It depends |
Test Items | Reactivity parameters | Test Items | Product performance |
Ratio of (A+C) and B material | 100/125~127 | Moulding density(g/cm3) | 0.25~0.35 |
Material temperature (oC) | 38~42/35~40 | Hardness(23ºC,Shore C/A) | 85~95C |
Cream time (s) | 5~8 | Tensile strength(MPa) | ≥3 |
End of rise time (s) | 20~30 | Elongation(%) | ≥100 |
Free rise density (g/cm3) | 0.11~0.15 | Tear strength(kN/m) | ≥15 |
Metal mold temperature (oC) | 45~55 | DIN DIN abrasion resistance(mm3) | ≤300 |
Demould time(min) | 3~4 |