Subject | Unit | Test Markup | Test Value |
Elongation at break | % | ASTM D-882 | ≥90 |
Tensile strength | MPa | ASTM D-882 | ≥60 |
Tear strength | N/mm | ASTM D-638 | ≥30 |
Bending strength | MPa | GB/T 9341-2008 | ≥90 |
Bending modulus | MPa | GB/T 9341-2008 | 2500 |
Hardness | R-Scale | ASTM D-785 | 90-110 |
VST | ºC | ASTM D-1525 | 135 |
Surface adhesion | Dynes/cm | ASTM D-2578 | ≥40 |
Density | g/cm3 | ASTM D-792 | 1.15-1.25 |
Dielectric Strength | KV/mil | ASTM D-149 | >1.7 |
Dielectric constant | - | IEC60250 | ≥3.0 |
Breakdown voltage | KV/mm | ASTM D-149 | >30 |
Thermal conductivity | V | ASTM D-3638 | 200 |
Volume resistivity | cm | ASTM D-257 | ≥1016 |
Surface insulation resistance | / | ASTM D-257 | ≥1014 |
Flame retardant grade | / | UL94 | >0.25mm:V-0 ≤0.25mm:VTM-0 |
Oxygen Index(@10mils) | % | ASTM D-2863 | 32 |
Water absorption | % | ASTM D-570 | ≤0.3 |
Thermal conductivity | W/(m*K) | ASTM D-5470 | 0.37 |