Typical value at 23ºC | Unit | Test standard | N2GF5 |
Symbol | ISO 1043 | PA66+25%GF | |
Density | cm³/g | ISO 1183 | 1.32 |
Viscosity | ml/g | ISO 307 | 145 |
Water absorption ratio, at 23ºC in water saturated | % | ISO 62 | 6 |
Water absorption ratio,Water saturated | % | ISO 62 | 1.9 |
Melting point,DSC | ºC | DIN 53 765 | 260 |
Melt volum flow rate,MFR | cm³/10min | ISO 1133 | - |
Melt temperature range,injection molding/extrusion | ºC | 280-300 | |
Mold temperature range,injection molding | ºC | 80-100 | |
Mechanical properties | |||
Tensile modulus | Mpa | ISO 527-1/-2 | |
Tensile strength, break | Mpa | ISO 527-1/-2 | 175 |
Tensile elongation, break | % | ISO 527-1/-2 | 4 |
Bending modulus | Mpa | ISO 178 | 7600 |
Bending strength | Mpa | ISO 178 | 260 |
CHARPY impact strength +23ºC | KJ/ | ISO 179/IeU | |
CHARPY notched impact strength +23ºC | KJ/ | ISO 179/IeA | 12 |
izod impact, notch | KJ/ | ISO 180/A | |
Thermal performance | |||
HDT, 1.8 Mpa under load | ºC | ISO 75-1/-2 | 245 |
HDT, 0.45 Mpa under load | ºC | ISO 75-1/-2 | |
CLTE, longitudinal/transverse ( 23ºC-80ºC) | 10-4/K | ISO 11359-1/-2 | 0.3 |
Thermal conductivity | W/(m.K) | DIN 52 612 | 0.33 |
Specific heat volume | J/(kg.K) | 1600 |