| Base film | PP | PET |
| Normal thickness | 2.0μm ~12.0μm | 1.9μm ~12.0μm |
| Margin type | Single, two margins | |
| Coating metal | Zinc-Aluminum alloy,Aluminum | |
| Coating side | Single,two sides | |
| Edge structure | Heavy edge | |
| Cutting type | Straight cut, wave cut | |
Properties | Unit | Typical value |
| Density | g/cm3 | 0.905±0.005 |
| Thickness | µm | 2.0 ~ 12 |
| Tensile Strength | MD (MPa) | ≥100 |
| Elongation at Break | MD (%) | 20~200 |
| Elastic Modulus | MD (MPa) | 2800 |
| Heat Shrinkage | MD (%) | ≤5 ( 120°C, 10min) |
| Wetting Tension | mN/m | 38 (Corona treated side) |
| Surface Roughness | µm | 0.08 |
| Melting Point | ºC | 172 |
| Volume Resistivity | Ω.m | >1015 |
| Break-dowm Voltage | V/µm | ≥350 ( 23°C, DC ) |
| Dielectric Constant | 2.2 (20ºC,1KHz) | |
| Dissipation Factor | ≤4×10-4 (20ºC,1KHz ) | |
| RC | ΩF | ≥5×104 |
Properties | Unit | Typical value | ||
| Density | g/cm3 | 1.4 | ||
| Thickness | µm | <5 | 5~12 | ≥12 |
| Tensile Strength | MD (MPa) | ≥84 | ≥108 | ≥120 |
| Elongation at Break | MD (%) | ≥22 | ≥33 | ≥44 |
| Elastic Modulus | MD (MPa) | 3500 | ||
| Break-dowm Voltage | V/µm | ≥200 ( 23°C, DC ) | ≥250 ( 23°C, DC ) | |
| Heat Shrinkage | MD (%) | ≤2.5 ( 150°C, 10min) | ||
| Surface Roughness | µm | 0.095 | ||
| Melting Point | ºC | 256 | ||
| Volume Resistivity | Ω.m | >1015 ( 23°C, Humidity 50%) | ||
| Dielectric Constant | 3.2 (20ºC,1KHz) | |||
| Dissipation Factor | - | ≤60×10-4 (20ºC,1KHz ) | ||
| RC | ΩF | ≥1×104 | ||