PA6 product introduction
Chinese name: Nylon 6
Aliases: Polyamide 6, Nylon 6, PA6          English Name: Polycaprolactam
Chemical formula: C6H13NO                   Molecular weight: 115.1735
Density: 1.13g/cm3
Appearance: Translucent or opaque milky white particles
Boiling point: 255°Cat760mmHg              Flash point: 102.2°C
Melting point: 215°C                       Shrinkage: 1%~1.5%
Relative value:2.42-2.47
Features: thermoplasticity, light weight, good toughness, chemical resistance and durability, etc.
Application: generally used in auto parts, mechanical parts, electronic appliances, engineering accessories, etc.

Project	Unit	Inspection methods	Standard
Relative viscosity		ISO 307 in 96% H2SO4	2.80±0.03
Moisture content	%	Brabender	≤0.05
Extract content	%	International	≤0.50
Melting point	ºC	ISO 3146	≥215
NH₂-Groups	mmol/kg	International	M±4
HO-Groups	mmol/kg	International	M±4
Chip size	mm		2.5±1
Dirty points ≥1mm	point/100g		≤5

Processing method: injection molding
Properties: Translucent or opaque milky white crystalline polymer
Properties: thermoplastic, lightweight, tough, chemical resistance and durability
Burning identification method: yellow flame on blue background, burning plant flavor
Density: (g/cm3) 1.14-1.15
Balanced water absorption: 3.5% Has good wear resistance, self-lubrication and solvent resistance.
Tensile strength: > 60.0Mpa
Elongation: > 30%
Bending strength: 90.0Mpa
Notched impact strength: > 5(KJ/m2)