Complaint
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max0.12 | Max 0.025 | Max 0.025 | Max 0.70 | Max 1.0 | 12.0~15.0 | Max 0.60 | 4.0~6.0 | Bal. | - |
| Max Continuous Service Temp | 950C |
| Resisivity at 20C | 1.25 ohm mm2/m |
| Density | 7.4 g/cm3 |
| Thermal Conductivity | 52.7 KJ/m@h@C |
| Coefficient of Thermal Expansion | 15.4×10-6/C |
| Melting Point | 1450C |
| Tensile Strength | 588~735 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |
| 20 | 100 | 200 | 300 | 400 | 500 | 600 | 700 | 800 | 900 | 1000 |
| 1 | 1.005 | 1.014 | 1.028 | 1.044 | 1.064 | 1.090 | 1.120 | 1.132 | 1.142 | 1.150 |