| Temperature | ºC | 160 | 150 | 135 | 120 | 115 |
| Time | hour | 2.5 | 3 | 5 | 14 | 20 |
| Storage temperature | ºC | 10 | 15 | 20 | 30 |
| Time | Month | 20 | 15 | 10 | 6 |
Technical Data:
| Test content | Unit | Standard Value | ||
| Thermal class | H | F | ||
| Volatile content | % | ≤ 2 | ||
| Loss of weight at calcination | % | 26±2 | ||
| Soluble resin content | % | ≥ 90 | ||
| Tensile strength before curing | N/cm | ≥1500 | ≥1000 | |
| Maximum pull while banding | N/cm | 800 | 800 | |
| Tensile strength of ringlike sample at room temperature after curing | Mpa | 20ºC | ||
| above :900 | above :900 | |||
| Tensile strength of ringlike sample at working temperature after curing | Mpa | 180ºC | 150ºC | |
| ≥600 | ≥560 | |||
| Proof tracking index | ≥500V | |||
| Arc resistance | S | ≥160 | ||
| Breakdown voltage parallel to layers | KV | normal condition:≥25 after soaked in water for 24 hours:≥10 | ||
| Thermosetting | OK | |||
| Loss of tensile strength after soaked in oil | ≤10% | |||
Package: