Od95*12 Soft Easy Machining Cocrmo Discs for Zirkonzahn

Min.Order: 2

Product origin: Tianjin, China

Infringement complaint:

Complaint

US$ 50 ~ 100

Description

The pre-Sintered Co/Cr blocks are intended for use in manufacturing individually designed dental restorations, which can be polished or veneered after milling and sintering. locks comprised of cobalt-chromium alloy are used.The blocks are initially manufactured in a partially sintered state; then, enlarged by the inLab CAD/CAM system, they are individually processed to specification, and finally, densely sintered Fragment These densely sintered single-unit products are then veneered and/or polished in the usual manner following reworking. The advantages include:
The speed of the process,
The high quality of work,
The safety of the process due to wet processing,
The clean, purely digital workflow

Typical Material Properties
Typical Material Properties
Constituents (%)	Co	65
	Cr	28
	Mo	5
	(Mn+Si+Fe)	<1
	Organic Binder(Disc)	~1
Density (Sintering)	g/cm³	8.1
Open Porosity	%	0
Hardness (Vickers)	Hv10	260
Bending(Flexural) Strength	Mpa	450
Young`s Modulus	Gpa	180
Coefficient of Thermal	*10^-6/K	14.5
Expansion( 25 - 500ºC) CTE	*10^-6/K	14.5