Description
Homogenized bauxite
Homogenized bauxite have the properties of stable homogeneous structure and excellent high-temperature performance, it is getting after calcined in rotary kiln with selected raw bauxite by the latest technology.
Homogenized bauxite process as follows:
Raw crude bauxite-----Test----Crushing-----homogenized ratio---wetting milling---stir in pool---filter pressing---shaping---drying---calcining -----crushing----screening---packing---Warehouse---delivery<
Main size of homogenized bauxite we have:
0-1mm, 1-3mm, 3-5mm, 100mesh, 120mesh, 150mesh, 200mesh, 325mesh
Main grade of homogenized bauxite we have:
Homogenized bauxite HB83 Al2O3 83%min,
Homogenized bauxite HB83 Al2O3 85%min,
Homogenized bauxite HB83 Al2O3 86%min,
Homogenized bauxite HB83 Al2O3 87%min,
Homogenized bauxite HB83 Al2O3 88%min,
Homogenized bauxite HB83 Al2O3 90%min,
Homogenized bauxite HB83 Al2O3 92%min,
| Item | Al2O3 (%) | Fe2O3 (%) | TiO2 (%) | K2O+Na2O (%) | Bulk Density (g/cm³) | Water Absorption (%) |
| HB82 | ≥82 | ≤2.0 | ≤4.0 | ≤0.60 | ≥3.10 | ≤1.5 |
| HB85 | ≥85 | ≤2.0 | ≤4.2 | ≤0.60 | ≥3.15 | ≤1.5 |
| HB86 | ≥86 | ≤2.0 | ≤4.4 | ≤0.60 | ≥3.20 | ≤1.0 |
| HB87 | ≥87 | ≤2.0 | ≤4.5 | ≤0.55 | ≥3.25 | ≤1.0 |
| HB88 | ≥88 | ≤2.0 | ≤4.5 | ≤0.55 | ≥3.30 | ≤1.0 |
| Item | Al2O3 (%) | Fe2O3 (%) | SiO2 (%) | TiO2 (%) | K2O+Na2O (%) | Bulk Density (g/cm³) | Water Absorption (%) |
| HB90 | ≥90 | ≤1.50 | ≤3.50 | ≤4.0 | ≤0.45 | ≥3.30 | ≤1.0 |
| HB92 | ≥92 | ≤1.20 | ≤2.50 | ≤3.0 | ≤0.45 | ≥3.35 | ≤1.0 |
| HB95 | 95±0.5 | ≤0.80 | ≤3.50 | ≤2.0 | ≤0.45 | ≥3.45 | ≤0.5 |