1.6mm Inconel625 Alloy wire Used in Home appliances
Introduction
Nickel Alloy 625 is used both for its high strength and outstanding aqueous corrosion resistance. The strength of Nickel Alloy 625 is primarily a solid solution effect from molybdenum and columbium. Nickel Alloy 625 has excellent weldability. The matching filler metals are often used for dissimilar metal joining and to weld the aqueous corrosion alloy.
It can Equivalent to: Tafa 71T, Sulzer Metco 8625
Surface Preparation
Surface should be clean, white metal, with no oxides (rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning. Recommended method of preparation is, to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Application
l Digesters
l Corrosion Resistance
l Oxidation and Heat resistant Coatings
l Protective coatings against corrosive gases, protection against scaling of conventional low-alloy steels, build up coatings for dimensional restoration.
Chemical composition:
Grade
Ni%
Cr%
Mo%
Nb+Ta%
Fe%
Alloy 625
Min 58
20-23
8~10
3.15-4.15
Max 5
Physical Properties
Grade
Density
Melting Point
Alloy 625
8.4g/cm3
1290°C-1350 °C
Typical Deposit Characteristics:
Typical Hardness
Bond Strength
Deposit Rate
Deposit Efficiency
Machilityineab
HRB 92
7000 psi
11 lbs /hr/100A
70%
Good
Standard Sizes & Packing:
Diameter
Packing
Wire Weight
1/16 (1.6mm)
D 300 Spool
15kg((33 lb)/spool
Other sizes can be produced by customers' requirement.