Blow Film Rotational Moulding Grade Virgin Polypropylene PP/ABS/HDPE/LDPE/LLDPE Plastic Resin Gruanle Powder Pellet

1. Basic information:
Products name: LLDPE granules, LLDPE resin, LLDPE raw material, Liner Low Density polyethylene
Virgin lldpe powder, lldpe rotational molding powder Grade: Virgin Grade, or recycled Grade
Cas Code: 9002-88-4
Density: 0.91~0.93

2. Application

1) For production of film, technical items for pipes, fittings, and packing means.
2) For extrusion packaging film, rope, woven bags, fishing nets, water pipes; Injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box;
3) extrusion blow molding containers, hollow products, bottles.

3. Packing &Shipping
1 Packing: 25kg/pp bag, 25kg/paper bag, 1000kg/jumbo bag, 500kg/super sack
2 Loading: 17mt per 20 foot container
3 Loading Port: Any China Port
4 Lead time: 20days

PROPERTY	UNIT	Data
Melt Flow Index	g/10min	≤1.0
Density	g/cm3	≤0.945
Tensile strength	Mpa	≥14.0
Elongation at break	%	≥600
Brittle temperature at low temperature	°C	≤-76
ESCR ,FO	H	≥500
Carbon Black dispersion	--	--
Tensile strength after thermal aging	Mpa	≥13
Elongation after thermal aging	%	≥500
Dielectric strength	Mv/m	≥25
Volume resistivity	Ω.m	≥1*1014
change rate of tensile strength  after weather aging environment of 0--1008h	%	±25
change rate of elongation  after weather aging environment of 0--1008h	%	±25
change rate of tensile strength  after weather aging environment of 504--1008h	%	±15
change rate of elongation after weather aging environment of 504--1008h	%	±15

 
  Rotational Molding Grade for Tank Use

Tests	Value	Unit
Melt Flow Rate (MFR)	3.2	g/10min
Density	0.939	g/cm3
Melting Point	127	°C
Tensile Yield Strength	21	Mpa
Tensile Strength at Break	28	Mpa
Elongation at Break	1,100	%
Flexural Modulus	750	Mpa
Brittle Temperature	<-60	°C