API 5L X56n Psl-2 Pipeline Pipe

Min.Order: 1
Product origin: Cangzhou, Hebei, China
Infringement complaint: complaintComplaint
US$ 550 ~ 850

Description
API 5L  PLS1   PLS2

Manufacturing Technique:
Cold Drawn Steel Pipe 
Hot Rolled Steel Pipe 
Hot Expanded Steel Pipe


Steel Grade:
B  X42  X46  X52  X56  X60  X65  X70

Size:
Outer Diameter: 1/8"-36"(10.3mm-914.4mm)
Wall Thickness: 1.2mm-80mm
Length: Random Length,SRL,DRL(4-14M)

End:pland ends beveled ends

Surface: Bare, Black,Lightly oiled, Hot dip galvanized,, Varnish coating/Anti rust oil, Protective Coatings, 3PE

Packing:Nude, Plastic/steel plugs in both ends, Hexagonal bundles of max. 2,000kg with several steel strips, Two tags on each bundle, Wrapped in waterproof paper, PVC sleeve, and sackcloth with several steel strips, Plastic caps.


Third party inspection:SGS, BV, Lloyds etc.
Standard Steel GradeChemical ComponentsMachanical Property
CMnCrMoPSNiCuTensile Strength (Mpa)Yield Strength(Mpa)
API Spec 5L PLS1  B≤0.28≤1.20≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥415≥245
X42≤0.28≤1.30≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥415≥290
X46≤0.28≤1.40≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥435≥320
X52≤0.28≤1.40≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥460≥360
X56≤0.28≤1.40≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥490≥390
X60≤0.28≤1.40≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥520≥415
X65≤0.28≤1.40≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥535≥450
X70≤0.28≤1.40≤0.50≤0.15≤0.030≤0.030≤0.50≤0.50≥570≥485
            
Standard Steel GradeChemical ComponentsMachanical Property
CMnCrMoPSNiCuTensile Strength (Mpa)Yield Strength(Mpa)
API Spec 5L PLS2BN≤0.24≤1.20≤0.30≤0.150.0250.015≤0.30≤0.50415-655245-450
X42N≤0.24≤1.20≤0.30≤0.150.0250.015≤0.30≤0.50415-655290-495
X46N≤0.24≤1.40≤0.30≤0.150.0250.015≤0.30≤0.50435-655320-525
X52N≤0.24≤1.40≤0.30≤0.150.0250.015≤0.30≤0.50460-760360-530
X56N≤0.24≤1.40≤0.30≤0.150.0250.015≤0.30≤0.50490-760390-545
X60N≤0.24≤1.40≤0.50≤0.500.0250.015≤0.50≤0.50520-760415-565
X65Q≤0.18≤1.70≤0.50≤0.500.0250.015≤0.50≤0.50535-760450-600
X70Q≤0.18≤1.80≤0.50≤0.500.0250.015≤0.50≤0.50570-760485-635