Complaint
| NAME | CONTENT(%) |
| Al2O3 | 99.3-99.5(99.7) |
| SiO2 | 0.3-0.5 |
| CaO+MgO | 0.2-0.3 |
| K2O+Na2O | 0.2-0.35 |
| Fe2O3 | <0.1 |
| OTHER | <0.05 |
NO. | Property | Unit | Alumina |
1 | Al2O3 | % | >99.3 |
2 | SiO2 | % | - |
3 | Density | g/cm3 | 3.88 |
4 | Water absorption | % | 0.01 |
5 | Cold compressive strength | MPa | 350 |
6 | 20ºC leakage rates | Torr/L.sec | <10-11 |
7 | Twisting in high temperature | mm | 0.2 allowed in 1600ºC |
8 | Bonding in high temperature |
| not bonded in 1600ºC |
9 | 20-1000ºC coefficient ofthermalexpansion | mm.10-6/ºC.m | 8.2 |
10 | Thermal conductivity | W/m.k | 25 |
11 | Electric insulation strength | KV/mm | 20 |
12 | 20ºCdirect current insulation resistance | Ohm/cm | 1014 |
13 | High-temperature insulation resistance | 1000ºC MΩ | ≥0.08 |
1300ºC MΩ | ≥0.02 | ||
14 | Thermal shock resistance |
| 4 times not cracked in 1550ºC |
15 | Maximum working temperature | ºC | 1800 |