Iron Oxide Red Coating Bm130 High Temperature Resistance 300 º C

Min.Order: 12

Product origin: Yulin, Guangxi, China

Infringement complaint:

Complaint

US$ 800 ~ 950

Description

Wuchang Pigment has been engaged in the production, R&D and sales management team of high performance iron oxide series products for more than 20 years. The senior managers are all from domestic iron oxide pigments production enterprises. At present, there are more than ten high-performance iron oxide inventions. The high-temperature resistant zinc iron yellow, coated iron yellow, ferromanganese black, low red and red pigments for lithium batteries have been produced in large quantities. At the same time, the food-grade products developed by the company have passed strict European Union testing, and all heavy metal indicators are superior to industry and food-grade control standards.

purpose
High temperature resistance is generally used in plastics, PPC, PPE and other plastic products, wood plastic, aircraft shell, various plastics, thermosetting plastics, thermoplastic, rubber products, tires, coatings, etc.

(High-temperature Resistant Grade Iron Oxide)
Color	Type	Temperature resistance	[Fe₂O₃(105ºC Fe₂O₃ (Drying at 105ºC)	Volatile at 105°C	)Water soluble matter(Hot extraction method)	Residue(45um)	pH value	Oil absorption (g/100g)	Heat resistant to 30min	Tinting strength(Compared with standard)
Zinc iron yellow	3950T	800°	≥65.0%	≤0.5%	≤0.5%	≤0.3%	5.0-8.0	25-35	ΔE≤2(800ºC)	95%-105%
Coated iron yellow	BM313	300°	≥65.0%	≤0.5%	≤0.5%	≤0.3%	5.0-8.0	25-35	ΔE≤2(300ºC)	95%-105%
Ferromanganese black	770T	700°	≥65.0%	≤0.5%	≤1.5%	≤0.3%	5.0-8.0	20-30	ΔE≤2(700ºC)	95%-105%
Coated iron oxide red	BM130	700°	≥85%	≤0.5%	≤1.5%	≤0.3%	5.0-8.0	20-30	ΔE≤2(700ºC)	95%-105%