Complaint
| Thickness | OD | Width | Length | Diameter | Inner Core |
| 6-150mic | 1.2-2.0 | ≤2350mm | 3000-36000m/r | ≤800mm | 76mm(3″),152mm(6″) |
| Test Item | Test Method | Unit | Standard | Test Results | ||
| Tension Strength | MD | GB/T 1040.3 | MPa | ≥120 | 136 | |
| TD | ≥200 | 262 | ||||
| Elongation Break | MD | GB/T 1040.3 | % | ≥180 | 165 | |
| TD | ≥65 | 59 | ||||
| Aluminum layer thickness | GB/T15717-1995 | Ω/ | ≤3 | 1.98 | ||
| Heat Sealing Strength | QB/T2358 | ºC,N/15mm | ≥8 | 115ºC(8.6N) | ||
| Haze | GB/T2410 | % | ≤5.5 | 1.04 | ||
| Friction coefficient | Static | GB/T 10006 | / | / | / | |
| Dynamic | / | ≤0.80 | 0.4 | |||
| Dyne(PVDC coated side corona treated) | GB/T 14216 | mN/m | ≥38 | 48 | ||
| Aluminum layer evenness | GB/T15717-1995 | % | ±13 | -8.82~10.72 | ||
| Moirture-vapor Transmission Rate | GB/T 1037 | g/(m2·24h) | ≤2.5 | 1.12 | ||
| Oxygen Transmission Rate | GB/T 19789 | cm3/(m2·24h·0.1MPa) | / | 72.56 | ||
| TECHNICAL DATA SHEET | ||||
| Item | Unit | Typical Value | Test Standard | |
Tension Strengrth | MD | Mpa (≥170) | 210 | ASTM-D882 |
| TD | Mpa (≥170) | 210 | ||
Elongation Break | MD | % (≥90) | 110 | ASTM-D882 |
| TD | % (≥90) | 110 | ||
Friction coefficient | Static | (≤0.65) | 0.5~0.65 | ASTM-D1894 |
| Dynamic | (≤0.55) | 0.45~0.55 | ||
| Uniformity of Aluminum | % (±15) | -7.25~+8.35 | GB/T15717-1995 | |
| Adhesion of Aluminum | N/15mm (≥1.5) | 2.0 | EAA TEST | |
| Aluminum Thickness | OD | 2.2 | GB/T15717-1995 | |
| Dyne (Metallized side) | mN/m (≥54) | 54 | ASTM-D2578 | |
| Moisture-vapor Transmission Rate | g/(m2·24h) (≤3.5) | 1.2 | ASTM-F1249 | |
| Oxygen Transmission Rate | cm³/( m²·24h·0.1MPa) (≤15.0) | 1.2 | ASTM-F1927 | |
| Specification | |||
| Width | Thickness | Inner Core Diameter | Length |
| ≤2700mm | 8~100mic | 76mm(3″),152mm(6″) | 6000m,12000m,18000m.24000m.36000m |