Building Material Concrete PP Fiber Polypropylene Fiber

Min.Order: 11

Product origin: Shijiazhuang, Hebei, China

Infringement complaint:

Complaint

US$ 1250 ~ 1300

Description

Polypropylene Fiber Concrete PP Fiber for Building Material

PP Fiber Concrete Grout Mortar Tile Adhesive Reinforcement

KELAIDE brand polypropylene fiber is made of 100% polypropylene raw material particles through hot extrusion and continuous manufacturing processes. All performance indicators have reached or surpassed similar imported products. Our factory and Tsinghua University jointly developed an organic fiber-modified polypropylene (PP) fiber specifically for mortar. After a special production process and surface treatment, the cross section is a three-leaf (Y) shape, with good mechanical properties. When mixed into the mortar, it has a uniform three-dimensional random distribution, with high dispersibility and strong holding power with the mortar. Reduce and delay microcracks caused by various factors such as creep, plastic shrinkage, syneresis, chemical shrinkage, temperature difference and load, etc., thereby significantly improving the crack resistance and impermeability of mortar products, making the mortar integrity and flexibility improved performance, continuity and durability.

Feature & Packing:
Feature:It has a small diameter and a large specific surface area; it has good dispersibility in cement-based materials, resistance to acid, alkali, salt and other chemical corrosion, high melting point, and non-toxic.

Packing:1.0 kg/bag

Application:
Improve the impermeability and crack resistance of mortar, ordinary concrete, and high-performance concrete.
Improve concrete frost resistance, fire resistance, impact resistance, wear resistance and workability.
It mainly changes the physical properties of concrete, and has good compatibility with cement, coarse and fine aggregates and other additives.

material ingredient	100% Polypropylene
specific gravitys(g/cm³)	0.91
equivalent diameter(µm)	27.69
breaking strength(MPa)	641
Fiber elastic modulus(MPa)	8.5x103
percentage of breaking elongation(%)	30
Appearance	Bundle monofilament
Length(mm)	3-25
Melting point	>160