Description
Soft magnetic alloys 1J85 / FeNi 85 / Ni80Mo5Mainly used in two areas for energy conversion and information processing
In the power industry, mainly in the high magnetic field has a high magnetic induction and low core loss of the alloy. In the electronics industry, mainly at low or medium alloy having a high magnetic permeability and low coercive force. At high frequencies shall be made on a thin strip or alloy higher resistivity. Usually with sheet or strip.
Chemical composition| composition | C | P | S | Mn | Si |
| ≤ |
| Content(%) | 0.03 | 0.02 | 0.02 | 0.3~0.6 | 0.15~0.3 |
| composition | Ni | Cr | Mo | Cu | Fe |
| Content(%) | 79.0~81.0 | - | 4.8~5.2 | ≤0.2 | Bal |
Heat treatment system| shop sign | Annealing medium | heating temperature | Keep the temperature time/h | Cooling rate |
1j85 | Dry hydrogen or vacuum, pressure is not greater than 0.1 Pa | Along with the furnace heating up 1100~1150ºC |
3~6 | In 100 ~ 200 ºC / h speed cooling to 600 ºC, fast to 300 ºC draw a charge |