Higher Quality Peek Tubes

Min.Order: 100

Product origin: Zhenjiang, Jiangsu, China

Infringement complaint:

Complaint

US$ 90 ~ 121.6

Description

PEEK extrusion tube
The PEEK tube manufactured with contunuous process solves the problem of height and the inside Shrinkage hole,which also can reduce the cost during the CNC process. It is widely used for manufacturing sealing ring,piston ring,wearing bush and value seat in oil & gas,semiconductor industries.We extruded the larget PEEK pipe in China(OD590mm)

NO	Dimension(mm)	Weight(g)	Notes
1	Θ1.6θ0.131000	2.6	Unit(m)
2	Θ1.6θ0.251000	2.5	Unit(m)
3	Θ1.6θ0.51000	2.4	Unit(m)
4	Θ1.6θ0.751000	2.0	Unit(m)
5	Θ1.6θ1.01000	1.6	Unit(m)
6	Θ2.33θ1.61000	2.9	Unit(m)
7	Θ2.8θ2.51000	1.6	Unit(m)
8	Θ3.0θ2.671000	1.9	Unit(m)
9	Θ3.2θ1.01000	9.4	Unit(m)
10	Θ3.2θ1.61000	7.8	Unit(m)
11	Θ5.0θ2.51000	19.1	Squeeze
12	Θ5.0θ4.51000	5.8	Squeeze
13	Θ7.5θ4.01000	42.6	Squeeze
14	Θ10.2θ8.01000	40.9	Squeeze
15	Θ12.0θ4.01000	81.6	Squeeze
16	Θ12.45θ8.881000	77.7	Squeeze
17	Θ29.0θ18.01000	527.6	Squeeze
18	Θ39.0θ31.01000	571.5	Squeeze
19	Θ80.0θ30.01000	5612.8	Squeeze
20	Θ90.0θ40.01000	6633.3	Squeeze
21	Θ100.0θ50.01000	7653.8	Squeeze
22	Θ110.0θ60.01000	8674.3	Squeeze
23	Θ130.0θ60.01000	13572.7	Squeeze
24	Θ140.0θ80.01000	13470.6	Squeeze
25	Θ160.0θ90.01000	17858.8	Squeeze
26	Θ168.0θ132.01000	11021.0	Squeeze
27	Θ180.0θ110.01000	20716.2	Squeeze
28	Θ190.0θ130.01000	19593.6	Squeeze
29	Θ190.0θ140.01000	16838.3	Squeeze
30	Θ200.0θ130.01000	23573.6	Squeeze
31	Θ220.0θ150.01000	26431.0	Squeeze
32	Θ240.0θ170.01000	29288.4	Squeeze
33	Θ257.0θ230.01000	13418.6	Squeeze
34	Θ250.0θ190.01000	26941.0	Squeeze
35	Θ260.0θ210.01000	23981.8	Squeeze
36	Θ280.0θ210.01000	35003.2	Squeeze
37	Θ280.0θ230.01000	26022.0	Squeeze
38	Θ300.0θ250.01000	28063.8	Squeeze
39	Θ320.0θ300.01000	12654.2	Squeeze
40	Θ340.0θ250.01000	54188.6	Squeeze
41	Θ360.0θ280.01000	52249.6	Squeeze
42	Θ580.0θ450.01000	136645.0	Squeeze

PEEK main material grade and typical properties

Item	Test Standard	Unit	PEEK450G	PEEK450GL30	PEEK450CA30	PEEK450FC30
Item	Test Standard	Unit	100%PEEK	PEEK+30%Glass fiber	PEEK+30% Carbon fiber	PEEK+30% (Carbon fiber+Graphite+PTFE)
Color			Natural or Black	Natural or Black	Black	Black
Density	ISO1183	g/cm3	1.3±0.01	1.5±0.01	1.4±0.01	1.43±0.01
Water Abs(25ºC,24Hrs)	ISO 62	%	0.5	0.11	0.06	0.06
Mould shrinking percentage	3mm,170ºC Flow direction	%	1.2	0.4	0.1	0.3
Mould shrinking percentage	Perpendicular to flow direction	%	1.5	0.8	0.5	0.5
Melting point	DSC	ºC	343	343	343	343
Distortion temperature	ASTM D648	ºC	163	315	315	293
Continuous using temperature	UL 74685	ºC	260	260	260	260
Coefficient of thermal expansion	ASTM D 696	10-5ºC	2.2	1.5	2.2	4.7
Tensile strength(23ºC)	ISO527-2/1B/50	Mpa	100	155	220	134
Tensile elongation(23ºC)	ISO527-2/1B/50	%	34	2	1.8	2.2
Bending strength(23ºC)	ISO 178	Mpa	163	212	298	186
Compressive strength(23ºC)	ASTM D695	Mpa	118	215	240	150
Lzop impact strength(no gap)	ISO 180/U	KJ/m2	No break	51	46	32
Rockwell hardness	ASTM D785		103	107	102	99
Flammable level	UL 94	V-0@mm	1.5	1.5	1.5	0.75
Dielectric strength	IEC 248	KM/mm	18	19
Dielectric constant	IEC 250		3.2	3.2
Surface resistivity			10¹⁵	10¹⁵	3*10⁶	5*10⁶
Friction coefficient		µ	0.30-0.38	0.38-0.46	0.28	0.18